Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto. / Submitted by giuliana silveira (giulianagphoto@gmail.com) on 2016-03-23T16:54:51Z
No. of bitstreams: 1
TESE_RecristalizaçãoAçoInoxidável.pdf: 7424747 bytes, checksum: 802f4dafa228000280f221f001ab9dad (MD5) / Approved for entry into archive by Gracilene Carvalho (gracilene@sisbin.ufop.br) on 2016-03-23T17:25:34Z (GMT) No. of bitstreams: 1
TESE_RecristalizaçãoAçoInoxidável.pdf: 7424747 bytes, checksum: 802f4dafa228000280f221f001ab9dad (MD5) / Made available in DSpace on 2016-03-23T17:25:34Z (GMT). No. of bitstreams: 1
TESE_RecristalizaçãoAçoInoxidável.pdf: 7424747 bytes, checksum: 802f4dafa228000280f221f001ab9dad (MD5)
Previous issue date: 2015 / Os aços inoxidáveis ferríticos estabilizados ao Nióbio devem exibir boas propriedades de estampabilidade e qualidade superficial para aplicações em peças de formas complexas. Objetivando melhorar as propriedades mencionadas acima, a textura de solidificação deve ser modificada por recristalização. O presente trabalho investigou as condições termomecânicas mais favoráveis para promover a recristalização do aço 430Nb, principalmente a faixa de temperatura de laminação, durante a simulação da laminação a quente de acabamento em laminador Steckel.
Ensaios de torção a quente foram realizados para simular a laminação a quente de acabamento do aço 430Nb, em laminador Steckel. Variáveis importantes da laminação foram controladas durante a simulação: deformação e temperatura do passe, número de passes e tempo entre passes. O material utilizado nos ensaios foi de procedência comercial e os esquemas de simulação programados para reproduzir condições próximas às industriais. A caracterização microestrutural das amostras, antes e após a simulação, foi realizada por análises por microscopia ótica e EBSD,
A evolução da microestrutura foi investigada, com foco especial nos mecanismos de amaciamento e promoção de recristalização. As microestruturas foram analisadas por microscopia ótica e EBSD.
O mecanismo de amaciamento predominante foi a recuperação dinâmica, seguida de recristalização estática, sob as condições testadas em todas as simulações. A recristalização estática foi mais efetiva nas simulações realizadas nas faixas de temperatura entre 960-900ºC, 930-870ºC e 900-840ºC.
Os resultados dos ensaios de torção e EBSD mostraram que a simulação realizada na faixa de temperatura de 900-840ºC intensificaram a fragmentação da microestrutura. Esta faixa de temperatura é, portanto, indicada para otimizar o processo de laminação a quente industrial, de modo a contribuir para melhorar a qualidade superficial do aço inoxidável ferrítico 430 estabilizado ao Nióbio. _____________________________________________________________________________________ / ABSTRACT : Ferritic stainless steels stabilized with Nb should exhibit good properties as drawability and surface quality due to their use in applications for complex form components and good esthetic appearance, respectively. In order to improve the above mentioned properties, the solidification texture has to be modified by recrystallization. The present work investigated, within the restrictions of Steckel hot rolling schedule, which thermomechanical conditions, largely related to pass temperature, and would most favor SRX.
Hot torsion tests were performed in order to simulate the finishing hot rolling of a 430Nb steel, in Steckel mill. Important variables of the rolling were controlled during simulation: strain and pass temperature, number of passes and interpass time. The material used in the present work was supplied by APERAM and the simulations were established in order to simulate conditions similar to the ones apply by industry. The evolution of the microstructure was investigated by optical microscopy and EBSD, focusing especially on the softening mechanism and recrystallization promotion.
The main softening mechanism, under the tested conditions, for all simulations was dynamic recovery, followed by static recrystallization. The static recrystallization was more effective for the simulations performed at the range temperature between 960-900°C, 930-870°C and 900-840°C.
EBSD results showed that the simulation performed at the range temperature of 900-840°C increased the fragmentation of the microstructure. This range temperature was indicated to optimize the industrial hot rolling process, in order to improve the surface quality of the 430Nb steel.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:123456789/6342 |
| Date | January 2015 |
| Creators | Braga, Flávia Vieira |
| Contributors | Andrade, Margareth Spangler |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFOP, instname:Universidade Federal de Ouro Preto, instacron:UFOP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds