Programa de Pós-Graduação em Engenharia de Materiais. Departamento de Engenharia Metalúrgica, Escola de Minas, Universidade Federal de Ouro Preto. / Submitted by giuliana silveira (giulianagphoto@gmail.com) on 2016-03-04T16:28:51Z
No. of bitstreams: 1
DISSERTAÇÃO_SuscetibilidadeCorrosãoTensão.pdf: 3508598 bytes, checksum: 940f9e9c70d54093077592f79360b9a3 (MD5) / Approved for entry into archive by Oliveira Flávia (flavia@sisbin.ufop.br) on 2016-04-15T12:57:42Z (GMT) No. of bitstreams: 1
DISSERTAÇÃO_SuscetibilidadeCorrosãoTensão.pdf: 3508598 bytes, checksum: 940f9e9c70d54093077592f79360b9a3 (MD5) / Made available in DSpace on 2016-04-15T12:57:42Z (GMT). No. of bitstreams: 1
DISSERTAÇÃO_SuscetibilidadeCorrosãoTensão.pdf: 3508598 bytes, checksum: 940f9e9c70d54093077592f79360b9a3 (MD5)
Previous issue date: 2015 / Este trabalho foi realizado com o objetivo de se investigar o comportamento do aço
inoxidável duplex (AID) UNS S32304 em meios contendo íons cloreto, sob o ponto de
vista da corrosão sob tensão (CST). Para tanto, foram realizados ensaios de CST com
carga e deformação constantes. Os ensaios de CST com carga constante foram
realizados em soluções aquosas com 42% e 35%, em massa, de cloreto de magnésio
(MgCl2), em ebulição (143°C e 125°C, respectivamente). O ensaio de CST com
deformação constante dos eletrodos foi realizado com solução aquosa contendo 42%,
em massa, de MgCl2, também em ebulição (143°C). Foram realizados também ensaios
de polarização a fim de se avaliar o comportamento do aço em relação à corrosão por
pites. Microscopia óptica e análise química foram feitas para a caracterização do
material. Constatou-se a suscetibilidade à CST deste material, quantitativa e
qualitativamente, além da influência da concentração de íons cloreto na solução. Essa
comparação foi reforçada após a análise microfractográfica dos corpos de prova
ensaiados. Os ensaios de polarização potenciostática indicaram que o potencial de pite
foi por volta de 400 mVECS em solução aquosa contendo 3,5%, em massa, de cloreto de
sódio (NaCl). Por meio de microscopia eletrônica de varredura (MEV) constatou-se a
presença de alguns pites formados durante os ensaios de polarização. ________________________________________________________________________________ / ABSTRACT : work was carried out in order to investigate the duplex stainless steel UNS S32304
behavior in environments containing chloride ions from the point of view of stress
corrosion cracking (SCC). Thus, we performed SCC tests with constant load and
constant strain. SCC tests were carried out under constant load in aqueous solutions
with 42% and 35% by weight magnesium chloride (MgCl2), boiling (143 ° C and 125 °
C, respectively). The SCC test of constant strain of the electrodes was carried out with
an aqueous solution containing 42% by weight MgCl2, also boiling (143 ° C). Were also
conducted polarization tests in order to evaluate the steel about pitting corrosion
behavior. Optical microscopy and chemical analysis were performed to characterize the
material. It was found the susceptibility to SCC of this material, quantitatively and
qualitatively, beyond the influence of the concentration of chloride ions in the solution.
It was found susceptibility to SCC of this material, quantitatively and qualitatively,
beyond the influence of the concentration of chloride ions in the solution. This
comparison was reinforced after microfractographic analysis of test specimens. The
potentiostatic polarization tests indicated that the pitting potential was around 400
mVSCE in aqueous solution containing 3.5% by weight sodium chloride (NaCl). By
means of scanning electron microscopy (SEM) revealed the presence of some pits
formed under polarization tests.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:123456789/6398 |
| Date | January 2015 |
| Creators | Barros, Ramon Silveira Assis |
| Contributors | Cândido, Luiz Cláudio |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFOP, instname:Universidade Federal de Ouro Preto, instacron:UFOP |
| Rights | Autorização concedida ao Repositório Institucional da UFOP pelo autor, 01/03/2016, com as seguintes condições: disponível sob Licença Creative Commons 4.0, que permite copiar, distribuir e transmitir o trabalho, desde que seja citado o autor e licenciante. Não permite o uso para fins comerciais nem a adaptação desta., info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds