Previous issue date: 2013-02-28 / Capes / O presente trabalho tem como objetivo o estudo teórico/experimental da sorção de água
em compósitos poliméricos reforçados com fibras de macambira (Bromélia Laciniosa). Foi utilizado como matriz polimérica uma resina de poliéster insaturado e fibras de Macambira originárias do cariri paraibano. Os compósitos foram confeccionados com 70% de poliéster e 30% de fibras cortadas em tamanhos de aproximadamente 3 cm. Os ensaios de sorção de água foram realizados com amostras de 3 mm e 6 mm de espessura nas temperaturas de 25, 50 e 70°C. Uma modelagem matemática tridimensional transiente foi usada para predizer a transferência de massa durante a sorção de água destes compósitos. A cinética de sorção de água nos compósitos mostrou ser influenciada pela sua relação área/volume. Verificou-se que em tempos curtos, aproximadamente 50 horas, e temperatura de processo mais elevadas, os corpos com maior relação área/volume apresentam uma maior velocidade de sorção. Em tempos longos, os compósitos com maior relação área/volume e maior temperatura de processo apresentam maiores teores de água sorvida. O teor de umidade de equilíbrio dos compósitos com 30% de fibras de Macambira apresentaram valores de 16,8%, a 25°C, 17,00% a 50°C e 19,10% a 70ºC, para as espessuras de 3 mm, e de 12,5% a 25°C, 15,8% a 50°C e 14,8% a 70ºC, para a espessura de 6 mm. Resultados teóricos do teor de umidade médio dos compósitos foram comparados com dados experimentais e um bom ajuste foi obtido. Desta comparação, os coeficientes de difusão de massa foram obtidos para cada condição experimental. / This reseach aims to study theoretically and experimentally water absorption in polymer composites reinforced with macambira fiber (BromeliaLaciniosa). As polymer matrix was used unsaturated polyester resin and macambira fiber from cariri region of the Paraiba state. The composite samples were manufactured with 70% polyester resin and 30% macambira fiber (3cm length). Experiments were carried out in samples with 3 and 6 mm thickness at the temperatures 25, 50 and 70ºC. A transient 3D mathematical model was used to predict mass transfer during water sorption of the composites. It was verified that the water sorption kinetic is affected by area /volume relationships. For short time, approximately 50 h, the sample with lower area/volume relationships and higherprocess temperature presents a larger water absorption velocity, and for long times, these samples presents higher equilibrium water content. Equilibrium moisture content of the samples were 16.8% at 25ºC, 17.00%. at 50ºC and 19.10% at 70ºC, for 3 mm thickness, and 12.5% at 25ºC, 15.8% at 50ºC and 14.8% at 70 ºC, for 6 mm thickness. Predicted results of the moisture content of the composites were compared with experimental data, and a good agreement was verified. From this comparison diffusion coefficients were obtained for different experimental conditions.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1799 |
| Date | 25 September 2018 |
| Creators | CRUZ, Valério Carlos de Almeida. |
| Contributors | LIMA, Antonio Gilson Barbosa de., CARVALHO, Laura Hecker de., CARMO, João Evangelista Franco do., CAVALCANTI, Wilma Sales., NASCIMENTO, José Jefferson da Silva., BARBOSA, Enivaldo Santos. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | CNPq, CTPETRO, FINEP |
Page generated in 0.0025 seconds