Previous issue date: 2014-10-29 / O poli(cloreto de vinila) é muito utilizado em produtos para saúde para fabricação de
bolsas de sangue, tubos, cateteres, entre outros. Ele é obtido a partir da
polimerização do cloreto de vinila e pode ser processado por várias técnicas, como
extrusão, injeção, sopro, calandragem, etc. O poli(cloreto de vinila) é um material
rígido e instável termicamente e requer a adição de plastificantes, estabilizantes
térmicos e outros aditivos para fabricação de materiais flexíveis e resistentes. Neste
trabalho, foram caracterizadas mangueiras de PVC utilizadas como componentes
em produtos para saúde de cinco fabricantes diferentes, denominadas A, B, C, D e
E, com o intuito de avaliar suas características físico-químicas, morfológicas e
biológicas. As amostras foram caracterizadas por Difração de raios-X (DRX),
Espectroscopia na Região do Infravermelho com Transformada de Fourier (FTIR),
Microscopia Eletrônica de Varredura (MEV) com mapeamento por Espectroscopia
por Energia Dispersiva de Raios X (EDS), Análise Termogravimétrica (TGA), ensaios
mecânicos e de citotoxicidade. As análises foram realizadas no Laboratório de
Desenvolvimento e Avaliação de Biomateriais (Certbio). De acordo com os
resultados obtidos neste trabalho, pode-se concluir que todos os ensaios realizados
foram relevantes na caracterização das mangueiras, sendo que os resultados de
Espectroscopia na Região do Infravermelho com Transformada de Fourier
mostraram que todas as mangueiras são compostas por poli(cloreto de vinila) e por
plastificantes que possuem em sua estrutura anel aromático e grupamento éster. As
amostras A e B possuem características semelhantes entre si, entretanto,
mostraram-se bastante diferentes das amostras C, D e E. As amostras A e B, apesar
de serem mais espessas, apresentaram-se menos resistentes, mais viscoelásticas,
com menor cristalinidade e com maior estabilidade térmica, quando comparadas
com as amostras C, D e E. Contudo, não foi observada citotoxicidade nas
mangueiras, o que sugere que, dependendo da aplicação, todas as mangueiras
estudadas poderiam ser utilizadas em produtos para saúde. / Polyvinyl chloride is widely used in medical devices for the manufacture of blood
bags, tubes, and catheters, among others. It is obtained from the polymerization of
vinyl chloride and can be processed by various techniques such as extrusion,
injection molding, blow molding, calendering, etc. Polyvinyl chloride is a rigid and
thermally instable material that requires the addition of plasticizers, heat stabilizers
and other additives for making it a flexible and resistant material. In this work, flexible
PVC hoses used as components in medical devices from five different
manufacturers, named A, B, C, D and E, were characterized in order to evaluate their
physicochemical, morphological and biological characteristics. The samples were
characterized by X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy
(FTIR), Scanning Electron Microscopy (SEM) with mapping by Energy-Dispersive XRay
Spectroscopy (EDS), Thermogravimetric Analysis (TGA), mechanical and
cytotoxicity assays. The tests were performed at the Laboratory for Development and
Evaluation of Biomaterials (CERTBIO). According to the present results, it can be
concluded that all tests were relevant to the characterization of the flexible polyvinyl
chloride hoses, also the Fourier Transform Infrared Spectroscopy results showed that
all hoses are made of PVC and a plasticizer having aromatic ring and ester groups in
its structure. Samples A and B have similar characteristics however, they were quite
different from samples C, D and E. Samples A and B, although thicker, were less
resistant, more viscoelastic, have lower crystallinity and greater thermal stability
when compared with samples C, D and E. However, no cytotoxicity was observed in
the hoses tested, suggesting that depending on the application, all hoses studied
could be used in medical devices.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/358 |
| Date | 10 April 2018 |
| Creators | SERPA, Patrícia. |
| Contributors | FOOK, Marcus Vinícius Lia., PINTO, Maria Roberta de Oliveira., FOOK, Sayonara Maria Lia. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0014 seconds