Previous issue date: 2016-10-05 / Os blocos de concreto são os componentes mais importantes da alvenaria
estrutural, uma vez que eles são os principais responsáveis pela resistência à
compressão. Para que estes sejam de qualidade, a sua fabricação deve ser
realizada utilizando materiais com propriedades adequadas e procedimentos
de dosagem e cura controlada. A utilização de novos materiais na produção de
blocos de concreto estrutural vem crescendo em todo o mundo, e , com isso, a
possibilidade de utilizarem materiais alternativos, cuja principal preocupação é
o equilíbrio entre os aspectos ambientais, tecnológicos e econômicos. Assim,
este trabalho tem como objetivo principal avaliar o desempenho de blocos
estruturais de concreto simples com adição de Politereftalato de etileno (PET)
micronizado para uso na construção civil. Inicialmente as matérias-primas
foram submetidas às caracterizações físicas, químicas e mineralógicas, e em
seguida realizou-se o estudo da dosagem do concreto, objetivando-se
determinar o proporcionamento dos materiais e os teores de PET a serem
utilizados. Sequencialmente foram moldados blocos de concreto nas
dimensões de 14cmx19cmx29cm, com teores de 2,5%, 5,0%, 7,5% e 10% de
Politereftalato de etileno micronizado em substituição ao agregado miúdo para
a determinação das propriedades físicas e mecânicas. Observou-se que o PET
provocou o aumento da absorção e a redução do peso específico do concreto,
e que o teor de 2,5% resulta em valores de absorção que satisfazem os
requisitos normativos para blocos de concreto estrutural em que se utiliza
agregado normal ou leve. Para a resistência característica à compressão,
observou-se que o PET promoveu a redução da resistência do concreto, e,
quanto maior o teor de substituição, menor a resistência à compressão. No
entanto, para os teores de 2,5%, 5,0% e 7,5% de PET os valores obtidos para
a resistência característica permitiram classificá-los como blocos estruturais
classe B, com função estrutural, para uso em elementos de alvenaria acima do
nível do solo. Portanto, é viável, nos percentuais e nas condições estabelecidas
nesta pesquisa, sob o ponto de vista técnico, a utilização do Politereftalato de
etileno triturado em concreto para produção de blocos de alvenaria estrutural,
por possibilitar a obtenção de propriedades físicas e mecânicas que satisfazem
os parâmetros normativos. / The concrete blocks are the most important components of structural masonry,
since they are mainly responsible for the compressive strength. For these to be
quality, their manufacture must be carried out using materials with appropriate
properties and strength and controlled curing procedures. The use of new
materials in the production of structural concrete blocks has been growing
throughout the world, and with it, the possibility of using alternative materials,
whose main concern is the balance between the environmental, technological
and economic. This work aims to evaluate the performance of simple concrete
building blocks with the addition of polyethylene terephthalate (PET) micronized
for use in construction. Initially, the raw materials were subjected to physical
characterization, chemical and mineralogical, and then held the actual dosage
of the study, aiming to determine the proportioning of the materials and PET
content to be used. Sequentially were molded concrete blocks in the
dimensions of 14cmx19cmx29cm, at levels of 2.5%, 5.0%, 7.5% and 10% of
micronized polyethylene terephthalate replacing the fine aggregate for
determining the physical and mechanical properties. It was observed that the
PET caused the increased uptake and reduction of the specific weight of the
concrete, and that the content of 2,5% results in absorption values which satisfy
the regulatory requirements for structural concrete blocks which uses regular
aggregate or light. For the characteristic compressive strength, it was observed
that the PET caused a reduction of strength of concrete, and the higher the
replacement content, the lower the compressive strength. However, for contents
of 2.5%, 5.0% and 7.5% PET values obtained for the resistance trait enabled to
classify them as class B structural units, structural function, for use in masonry
units above ground level. Therefore, it is feasible, in percentages and conditions
set out in this study, from a technical point of view, the use of polyethylene
terephthalate triturated in particular for the production of masonry blocks, by
enabling obtaining physical and mechanical properties which meet the
normative parameters.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/952 |
| Date | 12 June 2018 |
| Creators | SILVA, José Bezerra da. |
| Contributors | RODRIGUES, John Kennedy Guedes., MENDONÇA, Ana Maria Gonçalves Duarte., LUCENA, Adriano Elísio de Figueiredo Lopes., CAVALCANTE, Erinaldo Hilário., NASCIMENTO, José Wallace Barbosa do. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0031 seconds