Previous issue date: 2015-07-09 / A técnica sling pela via transobturadora é eficaz para o tratamento de mulheres com
Incontinência Urinária de Esforço e apresenta elevada taxa de cura e melhora da
qualidade de vida com baixos índices de complicações. Este trabalho teve como
objetivo desenvolver e confeccionar, uma tela de policaprolactona, para uso na
técnica de Sling e realizar análises comparativas deste material com a tela de
polipropileno, utilizada comercialmente. A pesquisa foi desenvolvida no Laboratório
de Avaliação e Desenvolvimento de Biomateriais do Nordeste – CERTBIO. Utilizouse duas amostras de tela, uma confeccionada no CERTBIO e outra de uso
comercial. Foram avaliadas as composições químicas e físicas das telas de
Policaprolactona (PCL) e Polipropile no (PP), através das técnicas de:
Espectroscopia na Região de Infravermelho com Transformada de Fourier (FTIR),
Difração de Raios X (DRX) e Microscopia Eletrônica de Varredura (MEV), Tensão
superficial, Ensaios Mecânicos de Tração e Teste de Citotoxicidade. Pode-se
comprovar pela análise de FTIR, que o material formador das telas era apenas de
polipropileno e policaprolactona. A análise de DRX corroborou com os resultados
obtidos na análise de FTIR, que indicavam que o material das telas tratava de PP e
PCL, apresentando um espectograma característico d estes polímeros. Também,
através da análise de DRX, foi possível observar o grau de cristalinidade indicando o
PP que possui maior grau de cristalinidade que o PCL. Pode-se comprovar também,
que o PP possui maior resistência mecânica que o PCL, verificando assim que o PP
é mais frágil e quebradiço do que o PCL. A análise de tensão superficial mostrou
que as duas telas possuem molhabilidade parcial devido as cavidade presentes na
superfície das telas. A biocompatibilidade dos compostos foi confirmada com o teste
de Citotoxicidade. / The sling technique by transobturator approach is effective for the treatment of
women with Stress Urinary Incontinence and has a high cure rate and improved
quality of life with low complication rates. This work aimed to develop and produce,
polycaprolactone, screen for use in Sling surgery and to perform comparative
analyses of this material with a polypropylene bladder, used commercially. The
survey was developed in the laboratory of evaluation and development of
Biomaterials in the Northeast-CERTBIO. Two samples were used to screen; a made
in the laboratory and another used commercially. Been evaluated physical and
chemical compositions of the Polycaprolactone (PCL) and Polypropylene (PP)
screens, through the following techniques: infrared Spectroscopy in the region with a
Fourier transform (FTIR), x-ray Diffraction (XRD) and scanning electron microscopy
(SEM), surface tension, traction mechanical essays and Cytotoxicity test. You can
check by the FTIR analysis, that the trainer material of fabrics was just poliproplieno
and polycaprolactone, for examining the computer spectrogram. The XRD analysis
corroborated with the results obtained in the FTIR analysis, which indicated that the
material was PP screens and PCL, showing a characteristic you might like to look of
these polymers. Also, through the analysis of DRX, it was possible to o bserve the
degree of crystallinity indicating the PP has higher degree of crystallinity the PCL.
One can prove that the PP has higher mechanical strength than the PCL, checking
so that the PP is more brittle than the PCL. The analysis of surface tension showed
that both screens have partial wettability due to cavity present on the surface of the
canvas. The biocompatibility of the compounds has been confirmed with the
Cytotoxicity test and it showed low cytotoxicity in two screens.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/991 |
| Date | 14 June 2018 |
| Creators | COUTINHO, Carmem Lúcia Cavalcanti. |
| Contributors | NEVES, Gelmires de Araújo., FOOK, Marcus Vinicius Lia., PINTO, Maria Roberta de Oliveira., SILVA, Bartolomeu Jorge da. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds