Previous issue date: 2015-08-31 / Capes / Nos últimos anos, novos depósitos de argilas foram descobertos no Estado da
Paraíba, a caracterização destes depósitos é de fundamental importância para
estabelecer o melhor uso industrial dos mesmos. Neste contexto, o presente
trabalho teve como objetivo caracterizar argilas provenientes de jazidas do município
de Cubati-PB, visando estabelecer seus usos adequados como matérias-primas
cerâmicas. Para tanto, as matérias-primas foram submetidas às seguintes técnicas
de caracterizações: física, química, mineralógica e térmica. Posteriormente, foram
preparados corpos de prova por prensagem uniaxial a 19 MPa, estes foram secos
em estufa a 110°C, e submetidos a queima nas temperaturas de 750°C, 850°C,
950°C e 1150°C. Em seguida determinadas as propriedades físico-mecânicas:
retração linear de queima (RLq), absorção de água (AA), densidade aparente (DAp),
porosidade aparente (PA) e módulo de ruptura à flexão (MRF). As argilas A, B e C
são adequadas para uso em cerâmica branca e a argila D para cerâmica vermelha.
E todas as argilas contém composição mineralógica adequada para uso em
cerâmica vermelha. / In recent years, new clays deposits have been discovered in the state of Paraiba, the
characterization of these deposits is of fundamental importance to establish the best
industrial usage. In this context, the aim of this study was characterized clays in the
municipality of Cubati-PB, to establish their appropriate uses as ceramic raw
materials. Therefore, the raw materials were subjected to the following
characterization techniques: physical, chemical, mineralogical and thermal. Later,
specimens were prepared by uniaxial pressing at 19 MPa, before dry at 110°C, and
submitted to firing at temperatures of 750°C, 850°C, 950°C and 1150°C. It were
determined the physical and mechanical properties: linear firing shrinkage (LFS),
water absorption (WA), apparent density (DAp), apparent porosity (PA) and flexural
modulus of rupture (MRF). The clays A, B and C are suitable for use in white ceramic
and D to red ceramic. And all the clays contain adequate mineralogical composition
for use in red ceramic.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/994 |
| Date | 15 June 2018 |
| Creators | BRITO, Igor Pinheiro de. |
| Contributors | SANTANA, Lisiane Navarro de Lima., NEVES, Gelmires de Araújo., MACEDO, Reginaldo Severo de., ALMEIDA, Ester Pires de. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds