Submitted by Edisangela Bastos (edisangela@ufpa.br) on 2014-01-16T17:45:38Z
No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_SinteseCaracterizacaoAnalcina.pdf: 33941277 bytes, checksum: c51172c610eaca58f311dfd7a5a48bc8 (MD5) / Approved for entry into archive by Ana Rosa Silva(arosa@ufpa.br) on 2014-01-23T12:09:27Z (GMT) No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_SinteseCaracterizacaoAnalcina.pdf: 33941277 bytes, checksum: c51172c610eaca58f311dfd7a5a48bc8 (MD5) / Made available in DSpace on 2014-01-23T12:09:27Z (GMT). No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_SinteseCaracterizacaoAnalcina.pdf: 33941277 bytes, checksum: c51172c610eaca58f311dfd7a5a48bc8 (MD5)
Previous issue date: 2006 / Neste trabalho foi utilizado rejeito de caulim da região do Ipixuna-PA, com objetivo de sintetizar zeólita tipo analcina na forma sódica como fase cristalina predominante, através do processo hidrotérmico. O rejeito foi submetido à calcinação por 4 horas a 700°C, para
conversão em metacaulinita. A partir desta metacaulinita foi preparada uma mistura reacional
contendo diatomito e hidróxido de sódio, que foi levada à autoclave a uma temperatura de 215°C por 24 horas. Diversas variáveis do processo de síntese foram investigadas, entre elas destacam-se: disponibilidade de sódio, proporção de silício, natureza da fonte de sílica, pH na mistura reacional e tempo de autoclavagem. Isso com o intuito de se determinar quais asalterações que os produtos reacionais sofrem com tais modificações, definindo desta forma a
condição ideal de síntese da analcina. Foram avaliadas também algumas propriedades importantes do adsorvente, tais como: estabilidade térmica, onde foi aplicado o método de
Rietveld para identificar as modificações na estrutura cristalina; estabilidade em presença ácida; cinética de dessorção gerada pelo íon hidrogênio; comportamento das isotermas de adsorção de cobre, cádmio, zinco e níquel bem como avaliar a seletividade de tais cátions no adsorvente. A síntese de analcina mostrou-se possível usando rejeito de caulim. Quando analcina foi calcinada a 400°C foi observado deslocamento nos planos (h,k,l) e manteve-se
constante até 600°C, gerado pela saída de oxigênio da posição 1/8 da analcina, isso gera uma diminuição na célula unitária provocando uma diminuição nos canais e sítios ativos da zeólita
o que afetou a capacidade de adsorção. / In this work from kaolin processing industries from Ipixuna-PA were used in order to
synthesi analcime derived zeolite as predominant crystalline phase though the hydrothermal
process. The sample was converted into metakaolinite by calcinations at 700°C during 4
hours. From sample this metakaolinite a reacting mixture consisting of diatomite and sodium
hydroxide was prepared. In order to determine of ideal conditions for analcime synthesis, a
number of process variables were measured such as sodium availability, silicon ratio, nature
of the silica source, pH of the reacting mixture, and auto clave residence time. Some
important properties of the adsorbent where measured as well, such as thermal stability in the
presence of acids hydrogen desorption kinetics, the trends of the adsorption isotherms as such
as selectivity for copper, cadmium, zinc and nickel ions. Analcime synthesis from kaolin
processing wastes was feasible. A displacement in the (h, k, l) planes was observed at 400 °C
and was maintained up to 600°C, caused by the withdrawal of oxygen in positions 1/8 in
analcime, shrinking the unit cell and in active channels and sites of zeolite, affecting its
adsorption capacity.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/4642 |
| Date | 19 December 2006 |
| Creators | CORREA, Edinelson Saldanha |
| Contributors | NEVES, Roberto de Freitas |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Química, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds