Submitted by Edisangela Bastos (edisangela@ufpa.br) on 2015-02-25T20:45:08Z
No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_SintesePigmentosZeoliticos.pdf: 2987354 bytes, checksum: bcdc89d5f6a05a2e3c614ad465c6b2ce (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2015-02-27T15:35:24Z (GMT) No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_SintesePigmentosZeoliticos.pdf: 2987354 bytes, checksum: bcdc89d5f6a05a2e3c614ad465c6b2ce (MD5) / Made available in DSpace on 2015-02-27T15:35:24Z (GMT). No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_SintesePigmentosZeoliticos.pdf: 2987354 bytes, checksum: bcdc89d5f6a05a2e3c614ad465c6b2ce (MD5)
Previous issue date: 2013 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Pigmentos tipo ultramar foram sintetizados com sucesso a partir de zeólita NaA derivada de caulim e rejeito de caulim. Tal rejeito tem sido uma excelente fonte de silício e alumínio na síntese de zeólitas, por ser uma matéria-prima “natural” com alta concentração de
caulinita e baixos teores de impurezas, além do menor custo em comparação àquelas
matérias-primas industrializadas. A zeólita NaA derivada de tal rejeito apresenta características estruturais favoráveis a síntese de pigmentos ultramar, sua estrutura encapsula as espécies de enxofre formadas, que agem como cromóforos, e impedem que essas espécies
se oxidem e seja liberado elevados teores de gases tóxicos durante a reação. Zeólita NaA foi misturada com enxofre e carbonato de sódio em diferentes proporções com o objetivo de verificar a influência dessa variação na cor e na tonalidade dos pigmentos. Após calcinação a
500 °C por 5 horas os produtos foram caracterizados por DRX, FRX e Raman, além da classificação visual por cor e tonalidade por meio de fotografias. O resultado foi produtos com coloração que variaram do azul ao verde com diferentes tonalidades, ambas influenciadas pela
quantidade de aditivos, pela taxa de resfriamento após calcinação e pela granulometria. Assim, pode-se dizer que quantidades diferentes dos mesmos aditivos na mesma matriz zeolítica proporcionam aumento de intensidade da cor, que a taxa de resfriamento após
calcinação e granulometria da matriz zeolítica provoca mudança da cor. A partir de DRX foi observado que a estrutura da zeólita NaA não é transformada para o tipo sodalita, como normalmente observado na literatura. Por espectroscopia Raman foram identificadas as
espécies de enxofre responsáveis pela coloração no pigmento zeolítico, sendo: S6 2- o
responsável pela cor amarela e o S3- pela cor azul, e que a mistura dos dois resultou na cor verde, que predominou nesse trabalho. Por fim, o aproveitamento de rejeito de caulim na
produção de pigmentos zeolíticos parece ser uma boa proposta de produção sustentável. / Ultramarine pigments were successful synthesized from zeolite A obtained from kaolin
waste. This waste has been used as an excellent source of silicon and aluminum for zeolite
synthesis because of its high kaolinite concentrations and low contents of other accessory
minerals. The cost is naturally less than the industrialized product. The zeolite NaA derived
from kaolin waste presents characteristics favorable for synthesis ultramarine pigments, sulfur
species can be inserted inside the zeolite voids, which act as chromophores, and should
provide some protection against oxidation and avoids high levels of toxic gases during
reaction. Zeolite A was mixed with Sulfur and Sodium Carbonate in different proportions in
order to check the influence of this variation in color and shade of pigments. Further calcined
for 5 hs@500º C. They were characterized by XRD, XRF and, Raman in addition to visual
classification by color and shade. These products show colors from blue to green at different
shades, both influenced by the amount of additives, cooling rate after calcination and by
particle size. Thus, a different quantity of the same additives in the same zeolitic matrix
provides an increase in the color intensity, cooling rate after calcination and particle size
induces the color change. X-ray diffraction patterns showed that the structure of zeolite
NaA is not change in sodalite type as normally found in the literature. Raman spectroscopy
identified sulfur species responsible for color in zeolitic pigments. S6 2- is yellow and S3- is
blue and the mixture both is green, majority color in this work. Utilization the kaolin waste in
the production of zeolitic pigments is a good proposal for sustainable production.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/6363 |
| Date | 13 March 2013 |
| Creators | MENEZES, Raquel Aranha de |
| Contributors | ANGÉLICA, Rômulo Simões, PERGHER, Sibele Berenice Castellã |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Geologia e Geoquímica, UFPA, Brasil, Instituto de Geociências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds