Previous issue date: 2016-08-31 / A presente pesquisa teve como objetivo, investigar o efeito do teor de carbono e do
tamanho do abrasivo na resistência ao desgaste e no fenômeno de encruamento
superficial de quatro aços Hadfield. Para esse estudo, foi montado, o equipamento pino
contra disco, e, como abrasivo utilizou-se lixas de ferro, com o tamanho médio entre 36
µm e 93 µm. Para o alcance do objetivo proposto foram delimitados materiais e
métodos, a saber: (a) montagem do abrasômetro pino-disco a partir de um dispositivo
desativado disponibilizado pelo LFS-USP; (b) confrontar resultados experimentais –
dois materiais (Aço 1045 e alumínio 6351) foram submetidos a ensaios realizados na
UFPE e USP para fins de estudos comparativos; (c) avaliação da influência de
parâmetros do ensaio – três abrasivos com diferentes tamanhos de partículas e diferentes
cargas foram submetidos e avaliados mediante o desgaste abrasivo; (d) avaliação do
comportamento de diferentes composições do aço Hadfield perante ensaios de
abrasividade – aços contendo quatro diferentes teores de carbono foram submetidos a
ensaios com lixas #220 e #320; (e) análise das superfícies desgastadas – após os ensaios
dos materiais, as superfícies foram realizadas análises por microscópio eletrônico de
varredura (MEV) das superfícies desgastadas. Os resultados obtidos com o equipamento
na metodologia empregada tiveram uma boa reprodutibilidade. Foram observadas
diferenças nos resultados entre os equipamentos da UFPE e da USP. Quanto a este
tópico, o desgaste abrasivo do aço Hadfield foi influenciado pelo teor de carbono
apresentando uma relação em que maiores teores demonstraram menor efeito de
desgaste, diferentes tamanhos de abrasivo ocasionam um efeito de encruamento
significativo, onde se observou o ganho de dureza em aços com menores teores de
carbono. Contudo, foi apresentada uma oscilação do efeito no abrasivo #320. As
micrografias revelaram microssulcos e microcortes provenientes do ensaio e não foram
observadas diferenças nas marcas de desgaste quando utilizados tamanhos diferentes de
partícula abrasiva. Ao final, chegou-se a conclusão de que os resultados obtidos
demonstram que o teor de carbono influência na resistência ao desgaste do aço e
consequentemente no encruamento superficial do aço. Observa-se também a influência
do tamanho do abrasivo e carga aplicada o ensaio. / This research aimed to investigate the effect of the carbon content and the size of the
abrasive in the wear resistance and surface hardening phenomenon four Hadfield steel.
For this study , has been assembled , the disc against pin device and abrasive was used
iron sandpapers, with average size between 36 m and 93 micrometers. To achieve the
proposed objectives were defined materials and methods, namely: (a) mounting the pindisk
abrasômetro from a disabled device provided by the LFS-USP; (b) comparing
experimental results - two materials (1045 steel and aluminum 6351) were submitted to
tests performed at university and USP for purposes of comparative studies; (c)
evaluation of the influence of the test parameters - Three abrasive particles with
different sizes and different loads were submitted and evaluated by the abrasive wear;
(d) assessment of the behavior of different steel compositions Hadfield before
abrasiveness tests - steels containing four different carbon contents were subjected to
tests with sandpaper # 220 and # 320; (e) analysis of the worn surfaces - after the tests
of materials different analyzes were performed by scanning electron microscope (SEM)
of worn surfaces. The results obtained with the equipment in the methodology
employed had good reproducibility. There were differences in results between the
equipment and the UFPE USP. On this topic, the abrasive wear Hadfield steel was
influenced by carbon having a relationship in which higher levels showed less wear
effect, different abrasive sizes cause a significant strain hardening effect, which was
observed gain hardness steel with lower carbon content. However, an oscillation of the
abrasive effect on the # 320 was presented. The micrographs revealed microssulcos and
microcuts from test and differences were observed in wear marks when using different
sizes of abrasive particle. In the end, came to the conclusion that the results show that
the influence of carbon content in the wear resistance of steel and consequently the
surface of the steel hardening. It is also observed the influence of abrasive size and load
applied to the test.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/18671 |
| Date | 31 August 2016 |
| Creators | OLIVEIRA, Marcelo dos Anjos |
| Contributors | http://lattes.cnpq.br/2569114755496581, SILVA, Flávio José da, ALVES, Kleber Gonçalves Bezerra |
| Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Engenharia Mecanica, UFPE, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds