Previous issue date: 2016-08-25 / A incorporação de resíduos diversos dentro de seus processos produtivos tem sido uma
tendência na construção civil, esse processo visa a diminuição dos custos de produção e da
deposição de resíduos no meio ambiente, dentro desta ótica as cinzas vegetais tem sido bastante
estudadas devido as suas possíveis propriedades pozolânica. Para este estudo foi utilizada a cinza
do bagaço da cana-de-açúcar (CBCA) proveniente do estado de Pernambuco, esse material foi
submetido a um processo de secagem em estufa a 100°C e um peneiramento para retirar matérias
contaminantes como folhas, madeiras e outros. O material foi dividido em quatro partes e
submetido a um processo de calcinação nas temperaturas de 300°C, 400°C, 500°C e 600°C e
chamadas de CB 300, CB 400, CB 500 e CB 600, a parte do material que não passou por esse
tratamento foi denominada de CAN. Posteriormente a CBCA passou por um peneiramento em
peneiras de malha #200 e #400 e a moagem em um moinho de bolas e por fim essas amostras
foram submetidas aos ensaios de caracterizações físicas (Área específica, BET (BrunauerEmmett-Teller)
e Massa específica) e caracterização química (D.R.X. e termogravimetria) e
ensaios de consistência e resistência a compressão. A existência de atividade pozolânica foi
testada através dos ensaios de D.R.X. e resistência a compressão segundo as normas da ABNT
NBR 5751 (2012). No ensaios químicos (D.R.X.) ficou constatada a possível existência de
atividade pozolânica do material estudado apenas nas cinzas moídas a sete horas, no ensaio de
resistência a compressão apenas as cinzas moídas a sete horas apresentaram desempenho
satisfatório. O estudo mostrou a importância do processo de moagem do material e de como o
mesmo influencia na atividade pozolânica, já o processo de calcinação teve resultados abaixo do
esperado principalmente nas temperaturas a partir de 500°C, já que as amostras apresentaram
resultados melhores nas temperaturas de 300°C e 400°C. / The incorporation of various waste in their production processes has been a trend in the
construction industry, this process is aimed at reducing production costs and waste disposal on
the environment, within this perspective plant ash has been widely studied because of its
potential pozzolanic properties. For this study we used sugar cane bagasse ashes (CBCA) from
the state of Pernambuco, this material was subjected to a drying process in oven at 100 ° C and
sieving to remove contaminating materials such as leaves, wood and others. The material was
divided into four parts and subjected to a calcination process at temperatures of 300 ° C, 400 ° C,
500 ° C and 600 ° C and calls CB300, BC400, BC500 and BC600, the portion of the material
which has not undergone this treatment was designated CAN. Subsequently the CBCA passed a
sieve of sieve mesh # 200 and # 400 and grinding in a ball mill and finally the samples were
subjected to physical characterization assays (specific surface area, BET (Brunauer-EmmettTeller)
and Mass specific) and chemical (DRX and thermogravimetry) and consistency tests and
compressive strength. The existence of pozzolanic activity was tested by the D.R.X. tests,
thermogravimetry and compressive strength according to ABNT NBR 5751 (2012). In chemical
assays (XRD and thermogravimetric analysis) was found to contain the reactivity of the material
studied compared to pozzolan reference metakaolin (TCM), as compared to compressive
strength testing only the ash grinded to seven hours (M7H) showed satisfactory performance.
The study showed the importance of the process of grinding the material and how the same
influence on the pozzolanic activity, since the calcination process results below mainly expected
at temperatures from 500 ° C, since the samples showed better results in temperatures 300 ° C
and 400 ° C.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/20407 |
| Date | 25 August 2016 |
| Creators | GÓES, Pablo Borba de Barros |
| Contributors | http://lattes.cnpq.br/4716724024622223, MELO NETO, Antônio Acacio de |
| Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Engenharia Civil e Ambiental, UFPE, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds