Previous issue date: 2009-08-24 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The 100% cotton fabric (CO)* treated with plasma of methane CH4 has direct application in all areas that needs of aqueous solutions repellent material like coatings and uniforms applied biomedical, aeronautics, and automobile between
others. 100% cotton fabric (CO) samples were treated by plasma with two differents atmosphere: Methane gas (CH4), treatment time was varied in 10 in 10 min. until 60 min., and mixture methane/argon (CH4/Ar), it was varied the proportion 1:9, 2:8, 3:7, 4:6, 5:5, 6:4, 7:3, 8:2 e 9:1, with treatment time of 30 minutes. In both, the fluxe was 5 sccm (second cubic centimeter), pressure 6 mbar, voltage 490 V and current
0,15A. The objective of work was measure the superficial tension of 100% CO then it treated with plasma, using contact angle measures of water and glycerol with the
surface. The samples were tested after treatment, with 8 and 12 months to verify the superficial modification effects. It was verified an increase of hydrophobility with the Sessile drop values varied between 116,69? to 137,85? and it carried on after 12 months. The no treated samples shows contact angle equal 0?. OES analysis and Raman spectroscopy were accomplished. In the SEM analysis was verified oligomers. The plasma treatment is correct environmental, It turning greater than conventional treatments / O tecido 100% Algod?o (CO)* tratado com plasma de metano (CH4) tem aplica??o direta em todas as ?reas que necessitam de um material com maior repel?ncia a solu??es aquosas, como revestimentos e uniformes aplicados a ?rea biom?dica,
aeron?utica, automobil?stica, entre outras. Amostras de tecido 100% CO foram tratadas com plasma utilizando duas atmosferas diferentes: g?s CH4, com tempos que variaram de 10 em 10 min. at? 60 min., e uma mistura de metano/arg?nio
(CH4/Ar), em propor??es 1:9, 2:8, 3:7, 4:6, 5:5, 6:4, 7:3, 8:2 e 9:1, durante 30 min. O fluxo utilizado nos dois processos foi de 5 cm3/s (cent?metro c?bicos por segundo), a
uma press?o de 6 mbar , voltagem de 490 V e corrente de 0,15 A. O objetivo do trabalho foi medir a varia??o da tens?o superficial do tecido 100% CO ap?s tratado com plasma; Utilizando medidas de ?ngulo de contato da ?gua e do glicerol com a superf?cie. As amostras foram testadas imediatamente ap?s o tratamento, com 8 e 12 meses, a fim de verificar a dura??o do efeito desta modifica??o superficial. Verificou-se um aumento da hidrofobicidade atrav?s dos valores do teste da gota s?ssil que variaram entre 116,69? a 137,85? e se mantiveram ap?s 12 meses; As amostras n?o tratadas apresentam ?ngulo de contato igual a 0?. An?lises de
espectroscopia de emiss?o ?tica (EEO) e espectroscopia Raman (ER) foram realizadas, bem como, an?lise de microscopia eletr?nica de varredura (MEV) a qual confirmou presen?a de olig?meros. O processo a plasma ? ambientalmente correto e se torna superior em compara??o aos tratamentos convencionais
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/15583 |
| Date | 24 August 2009 |
| Creators | Freitas, Duciane Oliveira de |
| Contributors | CPF:09621199468, http://lattes.cnpq.br/7441669258580942, Barros Neto, Eduardo Lins de, CPF:59545844434, http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4798645D3, Fook, Marcus Vinicius Lia, CPF:00000000012, http://lattes.cnpq.br/4149843752530120, Alves J?nior, Clodomiro |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Engenharia Mec?nica, UFRN, BR, Tecnologia de Materiais; Projetos Mec?nicos; Termoci?ncias |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.004 seconds