Previous issue date: 2014-08-18 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / Dentre os principais pigmentos, os materiais cer?micos que possuem a estrutura espin?lio AB2O4 v?m se tornando objeto de grande interesse cient?fico e tecnol?gico devido ? capacidade em acomodar diferentes c?tions em sua estrutura, permitindo diferentes tipos dopagens e, consequentemente, a obten??o de diferentes cores. Estudos sobre pigmentos cer?micos, atualmente, v?m sendo direcionados para o desenvolvimento de pigmentos est?veis e obtidos a baixas temperaturas e com maior reprodutibilidade. O objetivo do seguinte estudo ? a utiliza??o de pigmentos inorg?nicos para aplica??es em revestimentos cer?micos, tentando compreender quais par?metros influenciam na colora??o do pigmento nos esmaltes cer?micos. Pigmentos a base de CoCr2O4, CoAl2O4, Co0,8Zn0,2Cr2O4 e Co0,8Zn0,2Al2O4Co/Cr, foram sintetizados por uma rota qu?mica usando gelatina como precursor org?nico. Tais pigmentos foram caracterizados por An?lise termogravim?trica, Difra??o de raios X (DRX), Espectroscopia na regi?o do Infravermelho, Microscopia eletr?nica de varredura (MEV) Espectroscopia na regi?o do UV-Vis?vel e Colorimetria. Os resultados confirmaram a viabilidade da rota de s?ntese utilizada; com rela??o aos p?s sintetizados, Os pigmentos mostraram-se cristalinos e as fases desejadas foram obtidas a partir de 500oC, com um aumento da cristalinidade, assim como o tamanho m?dio de cristalito. Os pigmentos possuem tonalidades que v?o do verde ao violeta de acordo com as dopagens e suas temperaturas de calcina??o. / Ceramic pigments that own mainly the spinel structure AB2O4 are becoming a
matter of great scientific and technological interest due to the ability of
accommodate different cations in its structure, allowing different dopings and thus
obtaining different colors. Studies on ceramic pigments currently are being directed
to the development of stable and pigments obtained at low temperatures and with
greater reproducibility. This work aims at the use of inorganic pigments for
applications in ceramic tiles, investigating the influence of doping and calcination
temperature on the coloring pigments and ceramic glazes. the based pigments of
CoCr2O4, CoAl2O4, Co0,8Zn0,2Cr2O4 and Co0,8Zn0,2Al2O4 were synthesized by a
chemical route using commercial gelatin as organic precursor. The materials were
characterized by thermogravimetric analysis (TG), X-ray diffraction (XRD), infrared
spectroscopy (FTIR) spectroscopy scanning electron microscopy (SEM) in the UVVisible
region and colorimetry. The results confirmed the feasibility of synthesis
used, the route presented pigments crystal structures and the desired phases were
obtained from 500 ?C with increased crystallinity and the crystallite size. The
pigments have hues ranging from green to violet according to their doping and
calcination temperatures.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/19391 |
| Date | 18 August 2014 |
| Creators | Costa, Asenete Frutuoso da |
| Contributors | 06117988320, http://lattes.cnpq.br/3318871716111536, Paskocimas, Carlos Alberto, 06296687877, http://lattes.cnpq.br/2365059843175411, Gomes, Danielle Karinne Silva, 03008972438, http://lattes.cnpq.br/8614921107777981, Aquino, Fl?via Medeiros de, 05660333486, http://lattes.cnpq.br/5822416945469021, Pimentel, Patricia Mendon?a, 77858239449, http://lattes.cnpq.br/9303372770390061, Melo, Dulce Maria de Ara?jo |
| Publisher | Universidade Federal do Rio Grande do Norte, PROGRAMA DE P?S-GRADUA??O EM CI?NCIA E ENGENHARIA DE MATERIAIS, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds