Previous issue date: 2015-03-27 / Filmes finos de Co2FeAl (CFA) e tricamadas CFA/M/CFA, nas quais M ? Au
ou Ag, produzidos por magnetron sputtering em substratos de vidro e orientados
de MgO (100), foram investigados com ?nfase em suas propriedades estruturais,
magn?ticas est?ticas e din?micas, sendo estabelecida uma rota para produ??o de
ligas de Heusler na forma de filmes finos em substratos amorfos e orientados. Atrav?s
da an?lise de difra??o de raios-X, destaca-se a forma??o de estrutura cristalina
c?bica do CFA, com fase A2 (desordenada estruturalmente), onde os ?tomos se
distribuem aleatoriamente na rede. As medidas de magnetoimped?ncia foram realizadas
variando o ?ngulo de aplica??o do campo magn?tico externo e a corrente
de sonda com rela??o ? anisotropia. As medidas de VSM revelam, em algumas
amostras, a presen?a de um patamar ocasionado pela forma??o de sistema bif?-
sico. Por esse motivo, os resultados apresentaram efeitos de magnetoimped?ncia
assim?trica (AMI). Para filmes simples e tricamadas com espessura da camada
magn?tica igual a 500 nm, o efeito AMI ? mais pronunciado. Com o aumento da
espessura, apesar do comportamento bif?sico permanecer, os efeitos assim?tricos
come?am a diminuir. O comportamento magn?tico quasi-est?tico e din?mico ?
interpretado em termos das caracter?sticas estruturais das amostras produzidas.
Portanto, foi estabelecida uma rota para produ??o de ligas de Heusler na forma
de filmes finos, com fase estrutural A2 e devido ? desordem estrutural foi poss?vel
estudar os efeitos hister?ticos e assim?tricos de MI. / Thin films of Co2FeAl (CFA) and trilayers with CFA/M/CFA, where M is Au
or Ag, produced by magnetron sputtering onto glass and oriented (MgO (100))
substrates were investigated. The structural, magnetic static and magnetic dynamics
properties were analyzed by distinct experimental techniques. Through
X-ray diffraction was observed an A2 phase for the samples (completely disordered),
where the atoms are randomly located in the lattice. The static magnetic
behavior, in some samples, reveal a plateau behavior generated by a biphasic
system. The magnetoimpedance measurements were performed by varying the
angle between the external magnetic field and current with respect of anisotropy
direction. For this reason, the MI results show a asymmetric magnetoimpedance
(AMI) behavior. For the single and trilayers samples with 500 nm-thick, the AMI
effect is more evident in comparison with samples with 1000 nm-thick. Therefore,
in this work was stablished a route to produce Heusler alloy samples with A2
phase in thin film geometry onto amorphous and oriented substrates, and due
to structural disorder was possible to study the hysteretic and MI asymmetric
effects.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/19906 |
| Date | 27 March 2015 |
| Creators | Escobar, Vivian Montardo |
| Contributors | 93928254049, http://lattes.cnpq.br/2531075321550052, Feitosa, Carlos Chesman de Ara?jo, 51233789449, http://lattes.cnpq.br/1150673024968512, Schelp, Luiz Fernando, 37092073049, http://lattes.cnpq.br/8797015996750551, Sommer, Rubem Lu?s, 34174877068, http://lattes.cnpq.br/7705036710106784, Bohn, Felipe, Corr?a, Marcio Assolin |
| Publisher | Universidade Federal do Rio Grande do Norte, PROGRAMA DE P?S-GRADUA??O EM F?SICA, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds