Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2015. / Made available in DSpace on 2015-12-01T03:15:10Z (GMT). No. of bitstreams: 1
336281.pdf: 7004475 bytes, checksum: 4aa7e01e1256db38a8aa5a72b3a1e557 (MD5)
Previous issue date: 2015 / Este trabalho tem como objetivo investigar o comportamento estrutural à compressão da alvenaria de blocos estruturais cerâmicos considerando o preenchimento dos furos com a argamassa de assentamento, como componente integrante do sistema construtivo em alvenaria estrutural. Para atingir o objetivo do trabalho, realizou-se a análise das propriedades mecânicas dos prismas, correlacionando-as com as propriedades obtidas com a caracterização dos blocos, argamassas e grautes. Para tanto, a análise foi dividida em três Etapas: Referência, Argamassa Mista e Argamassa Industrializada. Para a moldagem dos prismas, utilizaram-se três blocos de geometrias distintas; três traços de argamassas mistas; três traços de argamassas industrializadas e três traços de grautes, com resistências distintas. Como conclusões gerais do trabalho, podem destacar as seguintes: para os prismas preenchidos, em ambas as etapas, o fator com maior influência na resistência à compressão dos prismas foi o bloco; para os prismas preenchidos e moldados com os blocos de 6 MPa, da Etapa Argamassa Mista, o aumento na resistência da argamassa não gera aumento significativo na resistência dos prismas, constatando-se que a utilização dos blocos de 6 MPa e a argamassa C (traço 1:1:6), como assentamento e preenchimento, demonstra-se como a melhor combinação de bloco-argamassa, pois além deste traço apresentar o menor consumo de cimento, esta série de prismas quando preenchida com argamassa apresenta aumento efetivo da carga de ruptura, no valor de 60%, viabilizando a utilização da técnica prescrita na norma ABNT NBR 15812-2 (2010); para os prismas preenchidos da Etapa com Argamassa Industrializada, somente os prismas moldados com os blocos de 6 MPa apresentam aumento significativo na resistência à compressão com o aumento da resistência das argamassas, onde a melhor combinação de bloco-argamassa ocorre para o prisma moldado com a argamassa industrializada de 10 MPa, que apresenta aumento efetivo da carga de ruptura, no valor 40,5%. Diante do exposto, observa-se que o aumento na resistência à compressão dos prismas com a utilização da argamassa como preenchimento estrutural evidencia a viabilidade de utilização desta técnica, desde que a escolha entre os componentes dos prismas seja adequada.<br> / Abstract : This study aims to investigate the behavior of structural masonry clay blocks in structural compression considering the filling of their holes with bedding mortar, as part of a constructive system in structural masonry. In order to achieve this aim, the mechanical properties of the prisms were analyzed in relation to the properties obtained with the characterization of the blocks, mortars and grouts. The analysis was separated in three stages: References, Mixed Mortar and Industrial Mortar. Three blocks with different geometries were used for molding the prisms, as well as three mixes of mixed mortar, three mixes of industrial mortar and three mixes of grout, with different strength. The following stand out as general conclusions: for the filled prisms, in both stages the factor with highest influence on the prisms' strength was the block; for the filled prisms molded with 6 MPa blocks, on the Mixed Mortar stage, increasing the mortar strength does not increase the strength of the prisms significantly, having that the use of 6 MPa blocks and C mortar (mix 1:1:6) as bedding and filling, is the best block-mortar combination, because aside from presenting the lowest consume of cement, this series of prisms presents a significant increase in failure strength when filled with mortar, with a value of 60%, which makes the use of the technique prescribed by the ABNT NBR 15812-2 (2010) standard viable. For the filled prisms in the Industrial mortar stage, only the prisms molded with 6 MPa blocks present significant increase in compressive strength when the strength of the mortars is increased, where the best block-mortar combination occurs for the prism molded with the 10 MPa industrial mortar, which presents significant increase in failure strength, with a value of 40,5%. Having these results, it is noticed that the increase in compressive strength of prisms using mortar as structural bedding evidences the viability of such technique as long as the choice regarding the components is adequate.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/156758 |
| Date | January 2015 |
| Creators | Nascimento, Marcio Rogério do |
| Contributors | Universidade Federal de Santa Catarina, Roman, Humberto Ramos |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 265 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0114 seconds