Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia / Made available in DSpace on 2012-10-26T11:31:47Z (GMT). No. of bitstreams: 1
301490.pdf: 1511420 bytes, checksum: 891faa4fd1dd59d3e530f0442fe8060e (MD5) / Este estudo avaliou a influência da espessura das paredes circundantes do preparo na resistência à fadiga de dentes restaurados com Inlays cerâmicas. Trinta terceiros molares humanos foram divididos em 3 grupos, de acordo com o preparo realizado: G1, paredes circundantes (vestibular e palatal) com 2 mm de espessura; G2, paredes circundantes com 1 mm de espessura; e G3, paredes circundantes com 0,5 mm de espessura. Todos os dentes foram restaurados com uma restauração cerâmica confeccionada por um sistema CAD/CAM (CEREC 3D) (Vita MarkII, Vita Zahnfabrik), cimentada adesivamente (RelyX ARC, 3M ESPE). Após armazenamento em água destilada a 37º C, os corpos de prova foram submetidos ao teste de fadiga sob seguinte protocolo: freqüência de 5 Hz; pré-carga de 200 N por 5 mil ciclos; seguidos por carregamentos crescentes de 400, 600, 800, 1000, 1200 e 1400 N por 30 mil ciclos cada. Os corpos de prova foram ciclados até a primeira falha (fratura com perda de fragmento do dente ou da restauração) ou até completarem 185 mil ciclos. Também foi analisada a formação de trincas nos dentes antes e após os testes, através de uma câmera digital montada com uma lente macro e flash circular. A taxa de sobrevivência dos grupos foi comparada através da curva de sobrevivência de Kaplan-Meier (p>0,05). Todos os corpos de prova completaram os 185 mil ciclos máximos sem a ocorrência de fratura. Os grupos 2 (1 mm) e 3 (0,5 mm) apresentaram maior número de trincas, porém estatisticamente não significante (p>0,05). Demonstrou-se que preparos dentais com paredes circundantes remanescentes menores de 2 mm (1 mm e 0,5 mm), suportaram ao protocolo de fadiga proposto, indicando um novo limite para os preparos para Inlays cerâmicos, sem que seja necessário a redução de cúspides. / The aim of this study was evaluated the influence of the thickness of the surrounding walls of the dental preparation (2.0 mm, 1.0 mm and 0.5 mm) in the fatigue resistance of tooth restored with ceramic inlays. Thirty human third molars were selected and divided into 3 groups, according to dental preparation carried out: G1, surrounding walls (buccal and palatal) with 2 mm remaining thick, G2, surrounding walls (buccal and palatal) with 1 mm remaining thick, and G3 , surrounding walls (buccal and palatal) with 0.5 mm remaining thick. All dental preparations were performed using a high speed hand-piece attached to prosthetic delineator, through a device that held the hand-piece always in the same position and diamond burs (no. 3131, normal, fine and extra fine grain) perpendicular to the occlusal surface of tooth. All teeth were restored with a restoration made by in-office CAD / CAM system (CEREC 3D) from a ceramic block (Vita MarkII, Vita Zahnfabrik), the ceramic were adhesively cemented with a dual-curing resin cement (RelyX ARC, 3M ESPE). After one week stored in distilled water at 37° C, the specimens were subjected to fatigue test under the following protocol: frequency of 5Hz, pre-load of 200 N for 5,000 cycles, followed by increasing loads of 400, 600, 800, 1000, 1200 and 1400 N for 30,000 cycles each. The specimens were cycled until the first failure (fracture with loss of a fragment of tooth or restoration) or even complete 185,000 cycles. Also was discussed the crack formation in the teeth before and after the tests, using a digital camera mounted with a macro lens and ring flash. The survival rate of the groups was compared using the Kaplan-Meier survival curves (p>0.05). All specimens completed the maximum of 185,000 cycles, without the occurrence of fracture. The results showed that survival rate was 100%, showing no differences between the survival curves of the groups tested. Groups 2 (1 mm) and 3 (0.5 mm) had a more incidence of crack, however, statistically not relevant. It was shown that dental preparations with remaining surrounding walls smaller than 2 mm (1 mm and 0.5 mm), endured the proposed fatigue protocol, indicating a new limit for ceramic inlays tooth preparations, without requiring the cusp reduction.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/96386 |
| Date | January 2012 |
| Creators | Shibata, Shizuma |
| Contributors | Universidade Federal de Santa Catarina, Machado, Renata Gondo, Araujo, Elito |
| Publisher | Florianópolis |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 104 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds