Previous issue date: 2011-08-03 / The aim of this work was the study of the microstructure and the wear resistance of two stainless steels, the ferritic-AIF with 27% Cr and the superduplex-SDM modified with boron (3.5% wt.), processed by spray forming. The rapid solidification promoted by this process has resulted in the formation of a new structure with refined grains and metastable phases. The deposits, weighing about 3.5 kg, were characterized by combination of scanning electron microscopy (SEM), hardness, micro hardness and wear resistance according to ASTM G65-04. The deposits of AIF and SDM showed more refined microstructure and higher hardness in respect to materials produced by conventional casting. The wear resistance of the SDM was higher than the materials tabulated in ASTM G65-04, namely, AISI D2 tool steel and Stellite 1016, while the AIF presented an intermediary value between these two materials. The addition of boron to the SDM is associated with the formation of borides and led to an increase in the hardness and wear resistance of this spray formed material. / O presente trabalho investigou a microestrutura e a resistência ao desgaste de dois aços inoxidáveis, o ferrítico-AIF com 27% de Cr e o superduplex-SDM modificado com boro (3,5% p), conformados por spray. A solidificação rápida promovida por esse processo resulta na formação de uma nova estrutura com grãos refinados e fases metaestáveis. Os depósitos, pesando aproximadamente 3,5 kg, foram caracterizados pela combinação de microscopia eletrônica de varredura (MEV), dureza, microdureza e resistência ao desgaste, conforme a norma ASTM G65-04. Os depósitos de AIF e SDM apresentaram microestrutura mais refinada e maior dureza em relação aos materiais obtidos por fundição convencional. A resistência ao desgaste do SDM mostrou-se mais elevada a dos materiais tabelados na norma ASTM G65-04, ou seja, aço ferramenta AISI D2 e Stellite 1016, enquanto o AIF apresentou valor de desgaste intermediário entre esses dois materiais. A adição de boro no SDM é associada à formação de boretos e conduziu a um aumento na dureza e na resistência ao desgaste desse material conformado por spray.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufscar.br:ufscar/847 |
| Date | 03 August 2011 |
| Creators | Beraldo, Leamar Guedes |
| Contributors | Bolfarini, Claudemiro |
| Publisher | Universidade Federal de São Carlos, Programa de Pós-graduação em Ciência e Engenharia de Materiais, UFSCar, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFSCAR, instname:Universidade Federal de São Carlos, instacron:UFSCAR |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds