Dissertação (mestrado)—Universidade de Brasília, Instituto de Física, Programa de Pós-Graduação em Física, 2016. / Submitted by Albânia Cézar de Melo (albania@bce.unb.br) on 2016-06-30T15:35:42Z
No. of bitstreams: 1
2016_AlbertoJoseMoreiraRocha.pdf: 2535560 bytes, checksum: fef3d65cd08359c9d071dc58b9a44c17 (MD5) / Approved for entry into archive by Marília Freitas(marilia@bce.unb.br) on 2016-07-28T11:03:15Z (GMT) No. of bitstreams: 1
2016_AlbertoJoseMoreiraRocha.pdf: 2535560 bytes, checksum: fef3d65cd08359c9d071dc58b9a44c17 (MD5) / Made available in DSpace on 2016-07-28T11:03:15Z (GMT). No. of bitstreams: 1
2016_AlbertoJoseMoreiraRocha.pdf: 2535560 bytes, checksum: fef3d65cd08359c9d071dc58b9a44c17 (MD5) / Neste trabalho foram produzidos filmes finos híbridos em matriz de poli(estireno)-bloco-poli(etileno-ran-butileno)-bloco-poli(estireno) SEBS e nanopartículas de óxido de ferro funcionalizadas com ácido oleico, por meio da técnica de spin-coating. Em uma primeira etapa, as nanopartículas de óxidos de ferro (diâmetro de 5,8 nm) foram sintetizadas por meio do método de coprecipitação química, e caracterizadas por meio das análises de espectroscopia Raman, UV-vis e no infravermelho, microscopia eletrônica de transmissão, análise termogravimétrica TG e medidas magnéticas. O coloide magnético formado por nanopartículas de óxidos de ferro funcionalizadas com ácido oleico dispersas em hexano foi misturado com a solução do copolímero SEBS preparada previamente para posterior deposição por spin coating. O estudo foi realizado em amostras de filmes depositados variando-se a concentração de partículas de óxidos de ferro e, como controles, foram preparados um filme casting, com a maior concentração de nanopartículas empregada, e o filme obtido com o copolímero. A caracterização dos filmes produzidos foi realizada empregando-se as técnicas de perfilometria, espectroscopias Raman e UV-vis, e medidas magnéticas. Os filmes apresentaram espessuras na faixa de 45 a 104 nm, a presença das nanopartículas no filme foi observada nos espectros Raman e de UV-vis, bem como nos resultados das medidas magnéticas. Os resultados mostraram também que os filmes apresentaram comportamento superparamagnético, indicando que as partículas de óxidos de ferro provavelmente não formam grandes agregados na arquitetura dos filmes. ________________________________________________________________________ ABSTRACT / In this study, hybrid thin films comprising oleic acid-coated iron oxide nanoparticles embedded in the SEBS [poly(styrene)-block-poly(ethilene-ran-butylene)-block-poly(styrene)] matrix were fabricated using spin coating approach. Firstly, the iron oxides nanoparticles (diameter 5,8 nm) were synthetized via chemical co-precipitation method and characterized by Raman, UV-vis and Infrared spectroscopy, transmission electron microscopy, thermogravimetry and magnetic measurements. The resulting magnetic colloid was mixed with a previously prepared solution of SEBS copolymer, and employed for the spin coating deposition. The study was performed in thin films fabricated with different concentration of iron oxides nanoparticles and, as a control film, a casting sample prepared with the highest concentration of nanoparticles employed and another comprising only the copolymer deposited by spin coating. The characterization of films was performed using perfilometry, Raman and Infrared spectroscopy, UV-vis and magnetic measurement. The prepared films present films thickness in the range from 45 to 104 nm. The presence of the nanoparticles within the films was probed by Raman and UV-vis spectrum, as well as through magnetic measurements. The results show that films exhibit superparamagnetic behavior, indicating that particles do not form big clusters in the film structure.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/21038 |
| Date | 29 March 2016 |
| Creators | Rocha, Alberto José Moreira |
| Contributors | Soler, Maria Aparecida Godoy |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds