2016_HerlysHernandoCanizarezTorres.pdf: 62083823 bytes, checksum: ea0812a9e62c9c0300d4df9961cfd3e0 (MD5) / Neste trabalho se apresenta uma metodologia para união de tubos pelo processo de soldagem com a deposição do passe de raiz. Na realização da soldagem de topo, externa e sem abertura de raiz, a altura da face de raiz é um fator fundamental para obter penetração total. Em alguns casos, mata-juntas (podem ser de cobre o de materiais cerâmicos) são usadas para evitar vazamentos de solda. Porém, o cobre pode ocasionar inclusões e corrosão, além de trazer muitas dificuldades no momento de instalação e gerar grandes custos em campo. Assim sendo, realizou-se uma análise do efeito da penetração utilizando-se o método de fase de nariz decrescente na soldagem de passe de raiz sem uso de cobre-junta nem abertura de raiz, para as seguintes posições críticas de soldagem: plana, vertical e sobrecabeça. A análise foi feita utilizando o processo de soldagem MIG/MAG por curto-circuito derivativo, GMAW-CMT (Gas Metal Arc Welding - Cold Metal Transfer), com arame AWS ER 70S-6 (1,2mm) e o gás de proteção Ar+25%CO2. O Planejamento Composto Central foi utilizado como ferramenta para a melhor organização dos testes e para análise dos resultados fez-se uma otimização utilizando a teoria de Desirability para múltiplas respostas, usando chapas planas de aço 1020 com chanfro estreito em U. Logo, valida-se esta metodologia de penetração completa em soldagem orbital de meia volta descendente em um tubo ASTM 106 por meio do processo de soldagem curto-circuito convencional com a ajuda da potência de soldagem mesurada. Os testes foram realizados com arames consumíveis de diâmetros 0,9 e 1,2 mm. Ensaios de macrografia mostraram os passes de raiz com bom aspecto visual e sem defeitos internos, sugerindo assim a possibilidade de execução da soldagem com penetração total. _______________________________________________________________________________________________ ABSTRACT / In this manuscript is presented a methodology to realize the pipe union by the welding process with the deposition of the root pass. In the butt welding execution external without open root, the height of the root face is a key factor for getting full penetration. Sometimes, copper-joints are used to prevent leaks. Though, copper can cause inclusions and corrosion, producing many troubles during the installation and generating large costs in the work area. Therefore, it was performed a penetration effect analysis using the slanted nose phase, method in root pass welding without the use of copper-joint or root opening, for the following critical welding positions: flat, vertical and overhead. The analysis was performed using the welding process MIG/MAG by derivative short circuit, GMAW-CMT (Gas Metal Arc Welding – Cold Metal Transfer), with AWS ER 70S-6 wires (1.2 mm) a with Ar+25%CO2, as shielding gas. The Central Composite Design (CCD) was used as a tool for a better organization of the tests, whereas to analyze the results it was made an optimization based on the Desirability theory for multiple responses, employing flat sheets of 1020 steel with a narrow-gap in U-shape. Then, this full penetration methodology in orbital welding turned down was validated in a ASTM 106 pipe through the conventional short-circuit welding process, with the joint established in the previous stages. The tests were performed with wires of 0.9 and 1.2 mm in order to evaluate the welding power. Macrography tests showed root pass with an acceptable visual appearance and without internal defects, thereby suggesting the possibility of welding execution with full penetration.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/21251 |
| Date | 25 May 2016 |
| Creators | Canizarez Torres, Herlys Hernando |
| Contributors | Alfaro, Sadek Crisóstomo Absi |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.0014 seconds