Previous issue date: 2007-03 / Medidas de magnetização, ressonância magnética do elétron e outras técnicas acessórias foram utilizadas no presente estudo para investigar uma amostra de fluido magnético não aquoso baseado em nitreto de ferro contendo cerca de 2×1016 partículas/cm3. Dados de microscopia eletrônica de transmissão indicam um formato esférico para as partículas, possuindo estas um diâmetro médio de 12,2 nm, com dispersão de 0,14. O espectro Mössbauer da amostra, a 77 K, indica a presença de 95% da fase γ’-Fe4N na amostra, com um resíduo de 5% da fase ε-Fe3N. A dependência com a temperatura da magnetização foi investigada sob a condição da amostra congelada inicialmente na ausência de campo (ZFC), no intervalo de temperaturas de 4 a 165K. Os dados ZFC foram ajustados usando-se uma abordagem que leva em consideração a dependência da anisotropia magnetocristalina com a temperatura, tornando a descrição da situação experimental mais realística. Espectros de ressonância do elétron foram ajustados, sugerindo informações sobre formação de aglomerados na amostra. _______________________________________________________________________________________ ABSTRACT / Magnetization measurements, electron magnetic resonance and other accessories techniques were used in the present study to investigate a non-aqueous ironnitride- based magnetic fluid (MF) sample containig about 2×1016 particles/cm3. The TEM micrographs indicated spherical-shaped iron nitride nanoparticles with an average diameter of 12.2 nm and diameter dispersity of 0.14. The 77K Mössbauer spectrum of the frozen MF sample indicated the presence of about 95% of the γ’-Fe4N phase, with a residual 5% of the ε-Fe3N phase. The temperature dependence of the magnetization was investigated under zero-field-cooled (ZFC) condition, in the temperature range of 4 to 165K. The ZFC-data were curve-fitted using a new approach that takes into account the particle size distribution and the temperature dependence of the magnetocrystalline anisotropy, making the description of the experimental situation more realistic. Electron magnetic resonance was fitted, providing some information about de clusters formation on the sample.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/3195 |
| Date | 03 1900 |
| Creators | Teixeira, Cimei Borges |
| Contributors | Morais, Paulo César de |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds