000792369.pdf: 1572222 bytes, checksum: fab5834775aa3e52a6906b27938cf02b (MD5) / Dois grupos de filmes finos foram feitos por polimerização em plasma, um a partir do HMDSN e outro a partir do C2H2 sob, respectivamente, uma pressão de 4Pa e de 10Pa e em um mesmo reator de aço inoxidável. A descarga foi excitada por rádio-frequencia (13,56MHz) durante 15 minutos para a polimerização a partir do C2H2 e 1 hora no caso do HMDSN. Posteriormente, esses filmes foram tratados por DBD produzida por uma fonte alternada (60 Hz) com pico de voltagem de 35kV. O tempo de tratamento para os filmes feitos a partir do acetileno foi de 1 a 5 minutos e de 2 a 10 minutos para os filmes a partir do HMDSN. Os filmes foram caracterizados quanto à estrutura molecular por meio de FTIR, a topografia por microscopia de força atômica e a molhabilidade por ângulo de contato. As medidas de ângulo de contato dos filmes feitos a partir do C2H2 após a exposição à DBD inicialmente apresentaram valores próximos de zero independente do tempo de tratamento. Posteriormente, esses valores aumentaram estabilizando em 30°, 45° e 54°, respectivamente, para 1, 3 e 5 minutos de tratamento. Esses valores são todos menores que o medido antes do tratamento, ou seja, 60°. Já no caso do HMDSN, o ângulo de contato médio, logo após o DBD, foi de 57°, 60° e 71°, respectivamente, para 5, 10 e 2 minutos de tratamento. Esses valores também aumentaram com o passar do tempo estabilizando próximo de 90° e abaixo dos 97° medidos antes do tratamento. Os espectros no infravermelho dos dois grupos de filmes indicaram alterações na estrutura molecular, contudo, sem a introdução de novos grupos funcionais. O filme feito a partir do C2H2 logo após a deposição apresentou uma rugosidade média igual a 64nm – menor que os 70nm do substrato. Com o aumento do tempo de tratamento, esse valor chegou a ser igual a 152nm. Já no caso do HMDSN, logo após a deposição ... (Resumo completo, clicar acesso eletrônico abaixo) / Two thin film groups were made by plasma polymerization from HMDSN at 4 Pa and C2H2 at 10 Pa. Both groups were made in the same stainless steel reactor. The discharge was produced by radio-frequency (13.56 MHz) during 15 minutes for polymerization from C2H2 and 1 hour for HMDSN. Thereafter, the films were exposed to DBD produced by an AC power supply at a frequency of 60 Hz with 35 kV of peak voltage. The time for treatment of films made from acetylene is from 1 to 5 minutes and from 2 to 10 minutes for films made from HMDSN. The film characteristics were evaluated from some techniques. Thus, molecular structure was characterized by FTIR, topography by atomic force microscopy and wettability by contact angle. After DBD exposure, contact angle measurements obtained on the films made from the C2H2 initially presented values close to zero no matter what the time for treatment was used. Thereafter, these values increased to 30°, 45° and 54°, respectively, for 1, 3 and 5 minutes for treatment. All these values are smaller than the ones measured before treatment (60°). After DBD, the films from HMDSN showed 57°, 60° and 71°, respectively, for 5, 10 and 2 minutes for treatment. As time went by, these values also increased to 90°, which is lower than measurements made before treatment (97°). The FTIR spectrum from two film groups showed changes in molecular structure, however without introducing new functional groups. After deposition, the films made from acetylene presented an average surface roughness equal to 64 nm, which is lower than the substrate surface (70 nm). As time for treatment increase, this value became equal to 152 nm. On the other hand, the films from HMDSN after deposition presented an average roughness equal to 4 nm for 5 minutes for treatment. After treatment, these films showed an average roughness equal to 15 nm for 7,5 minutes for treatment
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/111066 |
| Date | 24 June 2014 |
| Creators | Siqueira, Marcelo Barbosa [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Mota, Rogério Pinto [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 57 f. : il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0024 seconds