000863489.pdf: 2384161 bytes, checksum: 21b3016117fd918faa1b92c15a40eb86 (MD5) / A produção de aluminas com distribuição de tamanho e volume de poros controlados pela separação de fases líquido-sólido é um assunto emergente na área de cerâmicas porosas. As aluminas foram produzidas pelo processo sol-gel acompanhado de separação de fases, usando o óxido de polietileno (PEO) como agente indutor na separação de fases e o óxido de propileno para a gelatinização, para isso foram estabelecidas condições de controle cinético e termodinâmico desses eventos, através do controle do tempo de agitação e temperatura no meio reacional. Foram otimizadas rotas de síntese através do ajuste dos parâmetros de preparação variando a concentração do agente direcionador de poros PEO durante a transição sol-gel. Esta transformação foi acompanhada in-situ por SAXS revelando que o crescimento de objetos fractais com dimensionalidade de 1,7, que é característico do mecanismo e agregação controlado pela difusão. A calcinação em 700°C possibilitou a produção de aluminas da fase gama (-Al2O3) com textura porosa formada por macro e mesoporos. O uso do agente direcionador de poros PEO em proporção molar entre 0,01-0,07 mostrou-se eficiente no ajuste da macro-mesoporosidade. Entretanto quando se emprega proporções molares de PEO acima de 0,07 obtém-se apenas famílias de mesoporos com um decaimento do volume específico de poros quando a proporção molar aumenta de 0,08 para 0,1. Estas aluminas mesoporosas apresentaram maior área superficial especifica (Área BET máximo de 305 m²/g) e uma melhor relação OH/-O-Al em comparação com as macro-mesoporosas. / The production of alumina with volume and size distribution of pores controlled by phase separation induced by the addition of the polymer polyethylene oxide (PEO) during synthesis is an emerging issue in the area of functional ceramics. The aluminas were produced by the sol-gel process followed by phase separation, and the PEO as inducing agent phase separation and propylene oxide to gelation. Conditions for kinetic and thermodynamic control over these events were kept by controlling the stirring time and temperature in the reaction medium. Synthesis routes have been optimized by adjusting the preparation parameters varying the concentration of pores directing agent (PEO) during sol-gel process. This transformation was accompanied by in-situ SAXS and the results reveal the growth typical of fractal objects starting from a diluted solution, whose dimensionality in the Porod region was 1,7, characteristic of aggregation controlled by diffusion and the distances between the growing particles is around 2,95 nm. Gamma alumina (-Al2O3) with diversified porous texture and macro-mesopores was obtained with thermal treatment up to 700 ° C, being supported by several techniques. The macro-mesoporosity can be adjusted by PEO driver pores agent in a molar ratio from 0,01 to 0,07. Molar ratios of PEO above 0,07 produces only mesopores, decreasing the cumulative volume of this pores when the molar ratio increases from 0,08 to 0,1. These mesoporous aluminas had higher specific surface area (BET Area 305 m² / g) and better ratio OH/O-Al compared to the macro-mesoporous.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/138505 |
| Date | 16 October 2015 |
| Creators | Rodrigues, Jorge do Carmo [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Santilli, Celso Valentim [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 69 f.: il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0022 seconds