Previous issue date: 2017-02-06 / Cerâmicas à base de CaCu3Ti4O12 (CCTO) com estrutura perovskita ABO3 geraram grande interesse científico devido à descoberta da constante dielétrica (κ) gigante, propriedade não ôhmica elevada e propriedade fotoluminescente. Neste trabalho foram preparadas cerâmicas policristalinas na forma de pó com a seguinte composição: Ca1-xSrxCu3Ti4O12 (0,0 ≤ x ≤ 1,0) na qual o Ca2+ (sitio A) foi gradativamente substituído pelo cátion Sr2+. Foram analisados os efeitos desta substituição gradativa nas propriedades estruturais e microestruturais dos pós policristalinos. Mediante técnicas de análise termogravimétrica dos pós, produzidos por reação do estado sólido, determinou a temperatura de calcinação a 950ºC. Analisando as fases presentes no material por meio da técnica de difratometria raios X observa-se que a estrutura cristalina formada é do tipo perovskita. Ao realizar os estudos semi-quantitativos, mediante microscopia eletrônica de varredura com detector de energia dispersiva, se obteve a morfologia e composição química dos pós cerâmicos. Por meio das técnicas de espectroscopia (de infravermelho, de absorção ultravioleta-visível e de fotoluminescência) foram obtidos os valores 548 cm-1, 500 cm-1 e 415 cm-1, para os módulos vibracionais das ligações O-Ti-O, o band gap de 2,85 eV para as amostras estudadas e determinou-se as propriedades ópticas da cerâmica policristalina na forma de pó. / Ceramics made of CaCu3Ti4O12 (CCTO) create great scientific interest after the discovery of its giant dielectric constant (κ), the high non-ohmic property and photolumenescence. In this study were prepared polycrystalline ceramics in the form of powder with the following composition: Ca1-xSrxCu3Ti4O12 (0.0 ≤ x ≤ 1.0), in which Ca2+ (site A) was gradually replaced by a cation Sr2+. The effects of this graduated replacement were analyzed in the structural and microstructure properties of polycrystalline powders. By the thermogravimetric analysis of the powders, produced by solid state reaction, determined the calcination temperature at 1223K. Analyzing the phases present in the material by the diffraction technique of X-rays its observed that the crystal structure formed is perovskite. When conducting semi-quantitative studies, by the scanning electron microscope with energy dispersive spectroscopy, it was obtained the morphology and chemical composition of the ceramics powders. By the techniques of spectroscopy (infrared, ultraviolet-visible absorption and photoluminescence) were obtained the values 548 cm-1, 500 cm-1 and 415 cm-1, for the vibrational modules of the bonding O-Ti-O, the band gap of 2,85 eV for the studied samples and the optical properties of the powder polycrystalline ceramics were determined.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/150166 |
| Date | 06 February 2017 |
| Creators | Saska Junior, Luiz Antonio [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Angel Ramirez, Miguel [UNESP], Felix, Anderson André [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600 |
Page generated in 0.0018 seconds