paula_rfv_me_guara.pdf: 4489543 bytes, checksum: bf27a767025cebd5edeeb1ddec07b192 (MD5) / Este trabalho teve como objetivo estudar o efeito do jateamento e a diferença de três modos distintos de jateamento no comportamento em fadiga de molas de aço SAE 9254. Os seguintes métodos foram avaliados: molas sem jateamento; molas jateadas no processo P1 (jateamento a frio seguido de jateamento com a mola comprimida); molas jateadas no processo P2 (jateamento a quente seguido de jateamento com a mola comprimida) e molas jateadas no processo P3 (jateamento a quente seguido de jateamento com granalha fina). Foi avaliado o desempenho em fadiga das molas em três níveis diferentes de tensão aplicada, sendo que as molas para cada processo em estudo foram extraídas de um mesmo lote de arame. Foi observado que o método de jateamento P3 apresentou o melhor desempenho seguido do método de jateamento P2 e posteriormente do método convencional e o pior resultado foi das molas sem jateamento. Os resultados desta dissertação mostram que o jateamento pode aumentar de 3560 % a 15216 % a vida em fadiga das molas, dependendo do método de jateamento empregado, essa diferença no resultado do teste de fadiga é resultado do estado de tensões residuais compressivas na superfície das molas. A análise da fratura mostrou que o método de jateamento também influenciou no modo de falha das molas / The propose of this dissertation is to study the effect of shot peening method, comparing three different shot peening methods for suspension springs manufacture, it was performed fatigue test on the springs produced with steel grade SAE 9254. The following shot peening methods were evaluated: springs without shot peening; springs produced at P1 shot peening method (shot peening at ambient temperature followed by stress peening); springs produced at shot peening P2 method (hot shot peening followed by stress peening) and springs produced at shot peening P3 method (hot shot peening followed by shot peening with fine shot size). The fatigue tests were performed in three different stress levels, whereas all the springs used at this study are from the same lot. The P3 shot peening method, had a better fatigue life performance, followed by P2 shot peening method, the third better performance was the P1 shot peening method, and the worst results was the springs without shot peening process. It was concluded that the different results in fatigue life is due to residual stress condition at spring surface. The analysis performed at fracture origin showed that the springs broke due to different reason
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/94379 |
| Date | 26 June 2013 |
| Creators | Paula, Renan Felipe Vieira de [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Hashimoto, Tomaz Manabu [UNESP], Silva, Olivério Moreira de Macedo [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 145 f. il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1, -1 |
Page generated in 0.0022 seconds