Contribuição ao desenvolvimento de especificações por desempenho para concretos com escoria de alto-forno / Contribution to the development of performance specifications for concretes containing blast furnace slag

Orientador: Vanessa Gomes da Silva, Maristela Gomes da Silva / Acompanha 1 CD-ROM de Apendices e Anexo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo / Made available in DSpace on 2018-08-15T14:55:12Z (GMT). No. of bitstreams: 1
Ramadan_JussaraTanesi_D.pdf: 9121770 bytes, checksum: 922d5751838ca1dc378ab9d1297f680e (MD5)
Previous issue date: 2010 / Resumo: A produção anual de aço em 2008 foi de cerca de 31 milhões de toneladas O processo siderúrgico gera em média 500 kg de resíduos e co-produtos por tonelada de aço produzido. Desse total, 70% correspondem à geração das escórias. Investigar a possibilidade de moagem da escória de alto-forno para atender às usinas de concreto e indústrias afins é de vital importância como estratégia de sustentabilidade sócioambiental para a cadeia produtiva do aço e do concreto. No entanto, as atuais normas e especificações brasileiras de concreto se apresentam como um obstáculo para isso. Atualmente, a maioria das especificações de concreto é predominantemente prescritiva com alguns aspectos de desempenho. As especificações prescritivas impedem o uso de soluções mais inovadoras que potencialmente podem resultar em produtos com desempenho comparável ou até melhor do que aqueles que são produzidos de acordo com as especificações prescritivas. A solução para o avanço tecnológico é o uso de especificações por desempenho. As especificações por desempenho tratam do que se requer do produto e não prescreve como esse produto deve ser produzido. Em outras palavras, ao invés de partirem dos materiais que compõem o concreto, partem do desempenho desejado, deixando a seleção dos materiais, a dosagem e os métodos construtivos a cargo daqueles que contratualmente devem atender às especificações. Há uma necessidade crescente da inclusão de requisitos de desempenho nas especificações e normas, referentes à durabilidade do concreto, especialmente no que concerne a capacidade de proteção do concreto contra a corrosão da armadura. Isso requer que o desempenho da estrutura, ao longo da sua vida útil, possa ser estimado. Para isso, são necessários modelos de previsão de vida útil que correlacionem os requisitos e subrequisitos de durabilidade, medidos em laboratório por meio de ensaios acelerados, e o desempenho em serviço, obtido por meio de dados nas condições reais. Este trabalho apresenta um estudo laboratorial em concretos com escória de alto-forno, avalia suas principais propriedades, principalmente as relativas à deterioração referente à armadura. Foram avaliados: a retração, a absorção capilar, a resistência à compressão axial, o módulo de deformação, a carbonatação tanto natural quanto acelerada, a carga passante, a resistividade elétrica e o efeito sinérgico da carbonatação e da penetração de cloretos sobre a corrosão da armadura. Este efeito sinérgico foi avaliado por meio de ensaios cíclicos e a medida da profundidade de penetração de cloretos, da profundidade de carbonatação, da resistividade elétrica e do potencial de circuito aberto. Com os resultados obtidos neste estudo, verificou-se que a utilização de elevados teores de escória de alto forno, de maneira geral, ou não teve nenhuma influência ou exerceu uma influência positiva sobre as propriedades estudadas, com exceção da retração e da carbonatação acelerada. Os ensaios cíclicos apresentaram uma maneira de avaliar-se o efeito sinérgico da carbonatação e dos cloretos. Quando todos os resultados de ensaios acelerados cíclicos são comparados observa-se que, de maneira geral, as misturas com CP III-32-RS apresentaram o melhor desempenho no que concerne à corrosão das armaduras. Já os ensaios naturais não foram conclusivos. Além disso, este trabalho avalia a vida útil potencial desses concretos por meio da aplicação de modelos de previsão de vida útil. Independentemente do modelo utilizado para a previsão da despassivação por cloretos, a vida útil prevista aumentou com o aumento do teor de escória de alto-forno. De maneira geral, vida útil das misturas cresceu na ordem CPII-E-32, CP III-32-RS e CP III-32-RS + escória e com o aumento da classe de resistência. No entanto, observou-se que as recomendações da NBR 6118/2003 nem sempre garantem que a durabilidade da estrutura seja necessariamente atingida e não diferenciam misturas cujos desempenhos mostraram-se bem diferentes. As recomendações da NBR 6118/2003 mostraram-se inadequadas para a que uma vida útil mínima aceitável seja atingida. A partir desta avaliação de desempenho, apresentam-se sugestões para a modificação das especificações e normas brasileiras a fim de que sigam a tendência mundial e passem de prescrição ao desempenho. Diretrizes para a criação de especificações por desempenho de concretos com escória de alto-forno, incluindo sugestões para os requisitos e subrequisitos de desempenho, bem como os aspectos estratégicos, táticos e operacionais de sua implementação no Brasil também são apresentados / Abstract: In 2008 alone, the annual steel production in Brazil was around 31 million tons. The steel production process generates an average of 500 kg of residues and co-products per ton of steel. From this total, 70% corresponds to the slags. Although investigating the increase of blast furnace slag use is of extreme importance for the concrete and steel industries' socio-environmental sustainable strategy, the current Brazilian standards and specifications represent a barrier. Currently, most concrete specifications are predominantly prescriptive with some performance requirements. Prescriptive specifications prevent the use of innovative solutions that can potentially result in products with comparable or even better performance than those produced according to prescriptive specifications. The solution for the technology progress is the use of performance specifications. Performance specifications stipulate what is required from the product and do not prescribe how the product should be produced. In other words, they focus on the desired performance rather than on the concrete ingredients, materials selection, proportioning or construction methods. These are the responsibility of those individuals who contractually have to comply with the specifications. There is an increasing need to include performance requirements related to durability in specifications and standards, especially those related to reinforcement deterioration. It requires the performance of the structure to be estimated during its service life. It also requires service life prediction models which can correlate the durability requirements, measured through laboratory testing, and the performance in service, obtained from real exposure condition data. The present thesis presents a laboratory study on concretes containing blast furnace-slag, evaluates their main properties, especially those related to reinforcement deterioration. The following properties were evaluated: shrinkage, capillary absorption, compressive strength, modulus of elasticity, natural and accelerated carbonation, charge passed, electrical resistivity and the synergic effect of carbonation and chloride penetration on the reinforcement corrosion. This synergic effect was evaluated through cyclic testing and the measurement of chloride penetration, carbonation depth, electrical resistivity and open circuit potential. The results of this study showed that the use of high blast furnace slag contents generally either did not have an impact or had a beneficial impact on the properties studied, with exception of shrinkage and accelerated carbonation. The cyclic testing presented a way to evaluate the synergic effect of carbonation and chlorides. When all the accelerated cyclic test results are compared, it can be observed that in general the mixtures containing CP III-32-RS presented a better performance regarding reinforcement corrosion. On the other hand, the natural tests did not present any conclusive results. In addition, this thesis evaluated the potential service life of these concretes through mathematical models. No matter which model was used to predict corrosion initiation due to chloride ingress, the predicted service life increased with the increase of the blast furnace slag content. Generally, the service life of the mixtures increased in the order CPII-E-32, CP III-32- RS e CP III-32-RS + slag and with the increase of the compressive strength. Nevertheless, it was observed that NBR 6118/2003 recommendations do not always guarantee the structure durability and do not differentiate mixtures that performed considerably differently. NBR 6118/2003 recommendations were identified as inadequate to assure an acceptable service life. Based on the performance evaluation of the mixtures, changes to the Brazilian specifications and standards were suggested in order to follow the international trend and to move from prescription to performance. Guidelines to develop performance specifications for concretes containing blast furnace slag were presented, including suggestions for the performance requirements and sub-requirements. The strategic, tactic and operational aspects for their implementation in Brazil were presented, as well / Doutorado / Arquitetura e Construção / Doutor em Engenharia Civil

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/258512
Date02 October 2010
CreatorsRamadan, Jussara Tanesi
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Silva, Maristela Gomes da, Silva, Vanessa Gomes da, 1971-, Camarini, Gladis, Isaac, Ricardo de Lima, Matos, Oswaldo Cascudo, Sato, Neide Matiko Nakata
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Civil, Arquitetura e Urbanismo, Programa de Pós-Graduação em Engenharia Civil
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format319 p. : il. +., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0027 seconds