Estudo da precipitação de carbonetos e da fase sigma no aço inoxidavel tipo AISI 446 sob condições de trabalho em forno de radiação

Orientador: Paulo Roberto Mei / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-03T12:28:03Z (GMT). No. of bitstreams: 1
Guimaraes_AdilsonAntoninho_D.pdf: 25767273 bytes, checksum: c33643cf7ea34b13549c31a95275f014 (MD5)
Previous issue date: 2002 / Resumo: Foram estudados tubos de aço inoxidável AISI 446, utilizados em fomos de radiação na Usina de Processamento de Xisto da Petrobrás. Foram examinadas amostras de tubos novos e após o uso com o emprego de metalografia ótica, microscopia eletrônica de varredura, espectrometria por energia dispersiva, difração de raios-x, medidas de dureza (macro e microindentação) e dilatometria. Os resultados encontrados mostraram que os tubos novos apresentam carbonetos de cromo e uma amostra apresentou uma pequena quantidade de fase sigma. A quantidade de carbonetos e de fase sigma aumentou consideravelmente após o uso. O estudo da composição química das amostras em diversas posições nos possibilitou verificar uma carbonetação e sulfetação significativas nas amostras dos tubos usados. Esta carbonetação é diretamente responsável pelo aumento da quantidade de carbonetos. Foi possível ainda concluir que há uma diferença significativa de composição química de uma face do tubo para a outra, decorrente da distribuição de temperatura n(,) fomo. Em função desta diferença a carbonetação é muito mais acentuada na região mais quente. Os tubos usados foram submetidos a uma série de tratamentos térmicos, visando pesquisar a possível recuperação dos tubos, com reversão das fases formadas. Foi verificado que a fase sigma se dissolve a 900°C e os carbonetos a 1200°C. Nas condições estudadas o tratamento térmico por até 96 horas não causou a reprecipitação da fase sigma, confirmando que seu aparecimento só ocorre após longos tempos de exposição. A verificação das microestruturas resultantes após os tratamentos térmicos através da difração de raios-x mostrou que os carbonetos mudam de estrutura variando entre Cr2C, Cr3C2 ,Cr23C6 e Cr7C3 dependendo da posição no tubo e da área analisada. O efeito da carbonetação após o tratamento térmico foi de fazer surgir, para as temperaturas acima de 1100°C, a austenita, que em alguns casos se decompôs em perlita mais ferrita. Considerando que o aço AISI 446 é essencialmente ferrítico, a ocorrência da austenita é resultado do enriquecimento em carbono da matriz com o tratamento de solubilização.Visando caracterizar melhor a fase sigma foram fundidas amostras experimentais de Ferro-Cromo. Após laminação estas amostras possibilitaram a identificação inequívoca da fase sigma o que serviu de padrão para ser utilizado nas análises por difração de raios- x dos tubos de aços novos e usados / Abstract: Tubes of AISI 446 ferritic stainless steels used in a heating furnace of a Petrobrás petrochemical plant, were studied. Samples of brand new and used tubes were investigated using optical microscopy, scanning electron microscopy, energy-dispersive spectrometry, X-ray diffraction, hardness and microhardness measurements and dilatometry. It was found that under the working conditions the tubes were subjected to, precipitation of carbides and sigma phase occurs. The amount of carbides and sigma increased considerably after use. The chemical analysis of the samples in several positions made it possible to identify significant sulfidation and enrichment in carbon, in the used samples. This carbon enrichment is directly responsible by the increase in the amount of carbides. It was also possible to establish a significant difference in chemical composition from one side of the tube to the other, due to the temperature distribution in the furnace, in face of this difference, carbon enrichment is much more pronounced in one side than in the other. The tubes were also submitted to a series of heat treatment to check its effect in the components involved. It was seen that the sigma phase does dissolve at 900°C and the carbides also dissolve but at 1200°C. Under the conditions investigated, aging did not resulted in reprecipitation of sigma phase, thus confirm the sluggish nature of its precipitation. The x-ray diffraction results after heat treatment showed a change in structure of the carbides which can be Cr2C ,Cr3C2 ,Cr23C6 and Cr7C3 depending on the position of the sample in tube and the analysed area. The effect of carbon enrichment after heat treatment was sueh that the resulting microstructures after treating above 1100°C showed the presence of austenite which under some conditions decomposed to perlite plus ferrite. Taking in consideration that AISI 446 steel is essentially ferritic, the occurrence of austenite is the result of the matrix enrichment in carbon with the solubilizing treatment. Aiming to better characterize the sigma phase, iron-chrome samples were east in an experimental furnace. After rolling the samples the identification of sigma through x-ray diffraction was easy to be confirmed. / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263108
Date16 December 2002
CreatorsGuimarães, Adilson Antoninho
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Mei, Paulo Roberto, 1953-, Isore, Alain Jean, Cardoso, Lisandro Pavie, Zavaglia, Cecília Amélia de Carvalho, Santos, Rezende Gomes dos
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format154p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds