Orientadores: Rubens Caram Junior, Sergio Gama / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-23T15:57:36Z (GMT). No. of bitstreams: 1
Mota_MarilsaAparecida_M.pdf: 2948655 bytes, checksum: e2a5c838f65f3f962ba2cb717ae78092 (MD5)
Previous issue date: 1998 / Resumo: Ligas eutéticas constituídas por fases intermetálicas, com alto ponto de fusão, apresentam-se promissoras para aplicação industrial como materiais estruturais. Um sistema com potencial para a obtenção desses materiais estruturais é aquele formado pelos elementos Fe, Al e Nb, que apresenta estrutura eutética formada pela fase (FeAl)2Nb embebida na solução sólida (FeAl). Dependendo das condições de solidificação, a estrutura eutética pode ser alterada significativamente, o que permite exercer o controle da microestrutura final, para a obtenção de compósitos in situ. No presente trabalho, inicialmente realizou-se a análise do diagrama de fases Fe-Al-Nb, com o objetivo de determinar o vale eutético (Fe) + Fe2Nb para adições de Al entre 20 e 50% at. Em seguida, a influência da taxa de crescimento na microestrutura de solidificação foi analisada através da técnica de solidificação direciona! com aquecimento indutivo em atmosfera de argônio. Através da caracterização por microscopia óptica e eletrônica, duração de raios-X e análise térmica diferencial, foram obtidas estruturas eutéticas para as composições, Fe67Al22,8Nb9,7, Fe49,7Al41,2Nb9,1 e Fe47Al45Nb8. Finalmente, através da utilização de ensaios de compressão e dureza, foram avaliadas algumas propriedades mecânicas das ligas solidificadas direcionalmente / Abstract: Eutectic alloys formed by high melting point intermetallics phases, as in the case of the system formed with Fe, Al and Nb elements are promising material to be used as structural materials. This system presents eutectic structures formed by (FeAl)2Nb phase surrounded by (FeAl) solid solution. Depending on solidification conditions the eutectic structures can be significantly changed. This fact allows one to control the final microstructure, which permits to obtain in situ composites. In this work, firstly the analysis of the Fe-Al-Nb phase diagram was carried out. The aim of this study was to determine the eutectic valley (Fe) + Fe2Nb with of AI content from 20 up to 50 at.%. Following that, the influence of growth rate was investigated using the directional solidification technique, with inductive heating and under argon atmosphere. The eutectic structures compositions, Fe67Al22,8Nb9,7, Fe49,7Al41,2Nb9,1 and Fe47Al45Nb8, were determined using optical and scanning electron microscopy, x-ray diffraction and thermal analysis. Finally in order to evaluated the mechanical behavior of these eutectics, compression and microhardness tests of directionally solidified samples were performed / Mestrado / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263171 |
| Date | 16 March 1998 |
| Creators | Mota, Marilsa Aparecida |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Caram Junior, Rubens, 1958-, Gama, Sergio, 1949-, Mei, Paulo Roberto, Bolfarini, Claudemiro |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 80 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds