Orientador: Anselmo Eduardo Diniz / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-13T03:28:51Z (GMT). No. of bitstreams: 1
ArroyoOsorio_JoseManuel_D.pdf: 25100736 bytes, checksum: 163b1aa900bc2b44578e310b2fccbe2b (MD5)
Previous issue date: 2009 / Resumo: A usinagem é um dos processos de fabricação fundamentais da indústria contemporânea sendo o metal duro recoberto o material mais utilizado na fabricação das ferramentas de corte. A manufatura deste tipo de ferramentas inclui o processamento da superfície do substrato, previamente à deposição do recobrimento, com o objetivo de obter uma elevada resistência de aderência na interface substrato-recobrimento. O método mais difundido com este propósito e o jateamento do substrato com micropartículas de alumina que, embora amplamente utilizado e efetivo, gera poluição, risco à saúde do operador, consome muitos recursos de tempo e mão de obra e apresenta dificuldade no controle da rugosidade. Por outro lado a texturização a laser é uma tecnologia de engenharia de superfície baseada num laser pulsado que modifica a superfície do material através de fusão, evaporação, sublimação e subsequente solidificação. Nesta tese foi explorada a efetividade da texturização a laser como método alternativo ao jateamento na preparação pré-recobrimento da superfície do substrato. Este processo não apresenta poluição, permite o processamento seletivo de áreas especificas da ferramenta e, sendo automatizável, potencialmente utiliza menos recursos de tempo e mão de obra. As ferramentas selecionadas para experimentar foram duas classes de metal duro com recobrimento composto de TiCN+Al2O3+TiN depositado pelo processo MT-CVD, e, na preparação pré-recobrimento da superfície dos substratos experimentais foi utilizado um laser CuHBr pulsado. De acordo com a dinâmica do processo laser utilizado, é possível controlar a rugosidade do substrato e produzir uma grande diversidade de topografias e estruturas de superfície através da variação da intensidade e/ou da quantidade de pulsos do laser. Também foi verificado que o processamento com laser produz sempre transformações do WC, presente no substrato do metal duro, em novas fases não estequiométricas com menor teor de C. Por tentativa e erro, foram determinados dois conjuntos de parâmetros laser que produziram a melhor resistência de aderência avaliada através de ensaios de indentação: 02 pulsos, 410 MW·cm-2 e 64 pulsos, 239 MW. cm-2. Em ensaios de corte, tipo fresamento de topo a seco de aço molde P20 com ferramentas toroidais, foi comparado o desempenho de arestas microjateadas (comerciais) contra arestas texturizadas a laser (experimentais) encontrando uma vida média igual para ambos os tipos de arestas. Na análise detalhada dos mecanismos de desgaste foram encontradas em todas as arestas evidências de difusão, attrition, abrasão, deformação, delaminação, trincas e um mecanismo secundário, chamado desgaste por microfusão do material da aresta. Não houve diferenças notáveis entre as arestas comerciais e as experimentais que fossem atribuíveis ao processo de preparação da superfície do substrato para a deposição do recobrimento / Abstract: Machining is one of the fundamental manufacturing processes of contemporary industry and coated cemented carbide is the most used cutting tool material. Manufacturing of this kind of tools includes the substrate surface processing previously to coating deposition in order to achieve high adhesion resistance in the substrate-coating interface. The most spread out method with this intention is the substrate blasting with alumina micro-particles, which, although so widely used and effective, generates pollution, operator health risks, consumes considerable time and labor resources and presents roughness control difficulty. In the other hand, laser texturing is a surface engineering technology based on a pulsed laser which modifies the material surface through melting, evaporation, sublimation and subsequent solidification. This thesis aims to explore the laser texturing effectiveness as an alternative method for substrate surface pre-coating preparation. This process does not generate pollution, allows selective tool areas for processing and, being automated, it potentially requires less time and labor resources. The tools selected for the experiments were two kinds of coated cemented carbide with a composed TiCN+Al2O3+TiN MT-CVD coating and for the experimental substrate surface pre-coating preparation, a pulsed CuHBr laser was used. With the laser process dynamics used, it is possible to control the substrate roughness and to produce a great diversity of surface topographies and structures by adjusting the intensity and/or the amount of laser pulses. Also, it was verified that the laser processing always produces WC (present in the substrate) transformations in new non- stoichiometric phases with less C content. By trial and error method, two laser parameters sets were determined which produced the best adhesion resistance as evaluated through indentation tests: 02 pulses, 410 MW·cm-2 and 64 pulses, 239 MW·cm-2. In dry face milling cutting tests of mould P20 steel with toroidal tools, it was compared the performance of micro-blasted tools (commercial) against laser textured (experimental) ones finding an equal average life for both tool types. Detailed wear mechanisms analysis showed evidences in all the cutting edges of diffusion, attrition, abrasion, deformation, delamination, cracks and a secondary mechanism, called micro-melting wear of the material of the edge. There were no remarkable wear differences between the commercial edges and the experimental ones which could be attributable to the substrate surface pre-coating preparation process / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264151 |
| Date | 13 August 2018 |
| Creators | Arroyo Osorio, Jose Manuel |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Diniz, Anselmo Eduardo, 1959-, Machado, Álisson Rocha, Novaski, Olívio, Lima, Milton Sergio Fernandes de, Coppini, Nivaldo Lemos |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 168 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds