Orientador: Ramirez Londono, Antonio Jose / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-23T16:20:20Z (GMT). No. of bitstreams: 1
RodriguezFernandez_Johnnatan_D.pdf: 160902949 bytes, checksum: 4744bcf4bff982b6d8a31d0ccb36ea63 (MD5)
Previous issue date: 2013 / Resumo: Neste trabalho foram realizadas juntas soldadas dissimilares de aço ASTM A516 Gr 60 e da liga de Ni 625, com 6,6 mm de espessura, empregando o processo de soldagem por atrito com pino não consumível (SAPNC) conhecida em inglês como Friction Stir Welding (FSW). Juntas consolidadas foram obtidas com os parâmetros de soldagem de 300 rpm, 100 mm.min-1, 30 kN de força axial e o deslocamento tangencial (DT) de +2,0 mm. Dentre os parâmetros estudados encontrou-se que velocidades de rotação superiores de 300 rpm apresentaram um incremento dos defeitos volumétricos (vazios) e para velocidades menores de 300 rpm, observou-se uma relação entre a oscilação da ferramenta e o incremento das forças axiais. A avaliação da microestrutura foi realizada por meio de microscopia óptica e eletrônica de varredura e transmissão, espectroscopia de raios X dispersiva em energia (XEDS) e difração de elétrons retroespalhados (EBSD). Foi possível estudar a evolução microestrutural e entender as transformações de fases e mecanismos de recuperação e recristalização após o processo de SAPNC. No aço A516, o mecanismo de rearranjo e eliminação de defeitos cristalinos foi por recristalização dinâmica contínua e na liga de Ni observou-se que durante o processo ocorre recristalização dinâmica contínua e descontínua. Na interface entre o aço A516 e a liga Ni 625, com um tamanho de 2 ?m, foi observada a presença de precipitados do tipo NbC o que sugere que estes precipitados foram arrastrados desde a zona misturada. As simulações termodinâmicas dos precipitados durante o processo de soldagem encontram-se de acordo com as observações microestruturais. A análise mostrou texturas de cisalhamento simples em todas as regiões afetadas pela deformação durante o processo de soldagem. Além disso, foi possível determinar por meio das figuras de polo, as rotações das células cristalinas para atingir as orientações cristalográficas finais observadas na junta soldada a partir do estado inicial do material de base / Abstract: Dissimilar 6 mm thick butt joints of steel ASTM A516 Gr 60 and Ni-based alloy 625, were produced by friction stir welding (FSW). Fully consolidated joints were produced using rotational speed of 300 rpm, travel speed of 100 mm.min-1, tangent offset of 2.0 mm, and axial force of 30 kN. Among the parameters studied, it was found that rotational speeds higher than 300 rpm promoted an increase on the macro-voids size. On the other hand, rotational speeds lower than 300 rpm resulted on an undesirable and correlated tool and axial force oscillation. Microstructural characterization was performed using optical microscopy, scanning and transmission electron microscopy, energy dispersive X-ray spectroscopy (XEDS), and electron backscattering diffraction (EBSD). The microstructural evolution, phase transformations, and recovery and recrystallization mechanisms associated to the FSW process were investigated. In the steel A516, continuous dynamic recrystallization characterized by the rearrange and elimination of crystalline defects was identified as the main softening mechanism. In the Ni-based alloy, continuous and discontinuous dynamic recrystallization were the main mechanisms observed, with bulging of the original grain boundaries and progressive subgrain rotation. The NbC precipitates observed at the interface between the steel and the Ni-based alloy are thought to have been dragged from the Nibased alloy stir zone. Thermodynamic/kinetic simulations are in agreement with the above mentioned microstructural observation. The micro-texture analysis showed simple shear textures in all the welding zones affected by deformation during FSW. In addition, it was possible to determine the average crystalline cells rotations undergone by the base material to reach preferential orientations on the stir zone / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265064 |
| Date | 23 August 2018 |
| Creators | Rodriguez Fernandez, Johnnatan, 1983- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Ramirez Londono, Antonio José, Londono, Antonio Jose Ramirez, Button, Sergio Tonini, Mei, Paulo Roberto, Abreu, Hamilton Ferreira Gomes de, Santos, Dilson Silva dos |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 171 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0057 seconds