Orientador : Edison Bittencourt / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Campinas / Made available in DSpace on 2018-07-14T14:39:24Z (GMT). No. of bitstreams: 1
OrellanaRodrigues_LuisAlberto_M.pdf: 3814395 bytes, checksum: 1b09fdd92cb1c9dd6a2c541d9c295255 (MD5)
Previous issue date: 1985 / Resumo: Como resultado do interesse na investigação de métodos de tratamento superficial para aumentar a adesão, filmes de poliéster e polietileno foram irradiados com luz ultravioleta. Para estabelecer um estudo sistemático da modificação superficial destes materiais, os seguintes parâmetros foram escolhidos para sua caracterização: Ângulo de Contato, Energia Livre Superficial e suas Componentes, Força de Adesão e o Índice de Carbonila Normalizado obtida dos espectros de absorção do infravermelho. Todos os parâmetros foram relacionados com o tempo de exposição sob a radiação ultravioleta. As irradiações foram feitas na presença de ar e nitrogênio, como também com utilização do Diacetil, um foto-iniciador, aplicado na superfície dos filmes. A duração do tratamento superficial foi estudada através do índice de Envelhecimento, a diferentes temperaturas. Dos resultados obtidos experimentalmente foi observado que as mudanças superficiais dos filmes são semelhantes às obtidas com outros tratamentos tradicionais de superfície. A modificação foi mais eficiente nos filmes de poliéster e em qualquer caso mais fortes na presença do foto-iniciador. A componente polar da energia livre superficial foi o parâmetro chave para interpretar as mudanças nas propriedades de molhabilidade e adesão. A energia da superfície diminuiu com o tempo após a irradiação e este decréscimo é influenciado pela temperatura / Abstract: As the result of the interest in the investigation of methods of surface treatment of polymeric materials to increase adhesion polyester and polyethylene films were irradiated with ultraviolet light. In order to establish a systematic study of the surface modification of those materials, the parameter mentioned below were chosen for characterization of polymeric films: Contact Angle, Surface Free Energy and its Components, Force of Adhesion and Normalized Carbonyl Index obtained through measure of infrared absorption. All the measurements above were related to the time of irradiation with ultraviolet light. Irradiations were conducted in the presence of air, nitrogen, and also with Diacetyl, a photo-initiator, applied on the surface of the films. The durability of the treatments was studied by measuring its Aging Index, at differents temperatures. From the results obtained experimentally it was observed that the surface changes of the films were similar to those obtained with other surface treatments. The changes were more efficient with polyesters films, and in all case more strony in the presence of the photo-initiator. The polar component of the surface free energy v/as the key parameter to understand the changes in wetting and adhesion. The surface energy decreased with time after irradiations, and this decrease was affected by temperature / Mestrado / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267159 |
| Date | 10 May 1985 |
| Creators | Orellana Rodrigues, Luis Alberto |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Bittencourt, Edison, 1941- |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia de Campinas, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 116f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds