Orientador: Mario Antonio Bica de Moraes / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-07-26T03:43:23Z (GMT). No. of bitstreams: 1
Rangel_ElidianeCipriano_D.pdf: 787803 bytes, checksum: 0b3afb1a1012d775c5984bbf14f79319 (MD5)
Previous issue date: 1999 / Resumo: Neste trabalho, investigou-se a influência da implantação iônica sobre as propriedades de filmes finos de polímero depositados a partir de plasmas de radiofrequência (40 MHz, 70 W) de dois compostos orgânicos (acetileno e benzeno) e de suas misturas com gases nobres. As irradiações foram realizadas em um implantador iônico, com íons He+ , N+ e Ar+ , à fluências entre 1018 e 1021 íons/m2 e energias de 50 a 150 keV. As propriedades estruturais e ópticas dos filmes foram analisadas por espectroscopias no infravermelho e no ultravioleta-visível, respectivamente. Através de Ressonância Paramagnética de Elétrons, foi verificado que o bombardeamento iônico produz radicais livres na estrutura polimérica. A concentração destas espécies no filme foi investigada em função da energia e da fluência do feixe iônico. Variações nas concentrações dos elementos químicos presentes nas amostras com o bombardeamento iônico foram investigadas por Espectroscopia de Retro-espalhamento Rutherford. A espessura dos filmes foi medida com um perfilômetro, e associada aos dados obtidos por RBS, permitiu a determinação da densidade dos polímeros. Medidas de dureza dos filmes foram realizadas com a técnica de nanoindentação. Usando o método de duas pontas foi determinada a resistividade elétrica dos filmes e, através da exposição a plasmas de oxigênio, foi avaliada a resistência à oxidação. A interpretação dos resultados foi baseada nos perfis de perda de energia dos íons obtidos com o programa TRIM (TRansport of Ions in Matter) / Abstract: This work reports the influence of the ion implantation on the properties of thin plasma polymer films deposited from radiofrequency (40 MHz, 70 W) plasmas of two organic compounds (acetylene and benzene) and from their mixtures with noble gases. The irradiations were performed with an ion implanter, using He+, N+ and Ar+ ions, in the fluence and energy range of 1018 to 1021 ions/m2 and 50 to 150 keV, respectively. Infrared and ultraviolet-visible spectroscopies were employed to characterize the structural and optical properties of the films, respectively. Using Electron Paramagnetic Resonance spectroscopy, the formation of free radicals in the film structure was investigated as a function of the ion beam energy and fluence. Rutherford Backscattering Spectroscopy (RBS) was employed to determine the elemental composition of the samples and its change induced by the irradiation. Thicknesses of the films were measured with a profilemeter. Combination of the RBS and film thickness data allowed the determination of the density of the films. Hardness measurements were performed using the nanoindentation technique and the electrical resistivity of the films was determined by the two-point probe. The resistance to oxidation was determined from the etching rate of the polymers in an oxygen plasma. Interpretation of various experimental results were based on the implanted ion and energy loss simulation profiles, obtained with the TRansport of Ions in Matter ¿ TRIM code / Doutorado / Física / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/278415 |
| Date | 25 June 1999 |
| Creators | Rangel, Elidiane Cipriano |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Moraes, Mário Antônio Bica de, 1939-, Honda, Roberto Yzumi, Lepienski, Carlos Mauricio, Pagan, Cesar Jose Bonjuani, Machida, Munemasa |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 135p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds