Orientador: Mario Fernando de Goes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-11T04:18:14Z (GMT). No. of bitstreams: 1
Vaz_RicardoRodrigues_D.pdf: 6222625 bytes, checksum: 52f9da7090d419c4292ce5867fb19956 (MD5)
Previous issue date: 2008 / Resumo: O objetivo deste estudo foi avaliar in vitro a resistência e a morfologia da interface da união entre cimentos resinosos e dentina humana. A superfície oclusal de 20 terceiros molares foi removida e a dentina média preparada com lixa 600 de SiC. As restaurações de resina composta indireta (Sinfony) foram confeccionadas em formato circular com 2mm de espessura, jateadas com óxido de alumínio e silanizadas. Os dentes foram divididos em cinco grupos de acordo com a técnica de cimentação: Grupo I ¿ Rely X Unicem/com fotoativação, Grupo II ¿ Rely X ARC/Single Bond 2/com fotoativação, Grupo III ¿ C&B Cement/All Bond 2, Grupo IV ¿ Rely X ARC/Single Bond 2/sem fotoativação e o Grupo V ¿ Rely X Unicem/sem fotoativação. Após a cimentação os conjuntos dente/restauração foram armazenados em água destilada a 37oC por 24 horas e seccionados em formato de palitos com área quadrada de 0.8±0.2mm2 para o ensaio de tração nos tempos de 24 horas e 30 dias utilizando uma máquina de ensaios universal. O tipo de fratura foi observado e classificado em MEV (microscopia eletrônica de varredura). Os resultados foram submetidos à Análise de Variância e ao teste de Tukey para a comparação entre grupos e ao teste-t pareado para comparação entre os tempos de armazenamento de 24 horas e 30 dias (p<0,05). Para análise da morfologia da união em MEV foram obtidos discos de dentina com espessura de 2mm que após a cimentação conforme os grupos experimentais foram seccionados no sentido mesio-distal e incluídos em resina epóxi para os procedimentos de polimento e metalização. Os resultados revelaram que os grupos III, IV e V apresentaram aumento nos valores da resistência da união estatisticamente significantes no período de armazenamento de 30 dias. Os resultados da resistência da união em relação aos modos de polimerização nos tempos de armazenamento de 24 horas e 30 dias revelaram maiores valores na técnica de fotoativação. As análises dos padrões de fratura em MEV mostraram a predominância de fraturas coesivas no cimento para os grupos I e V nos tempos de 24 horas e 30 dias; para o grupo II houve predominância de fraturas mistas sendo coesivas no cimento, na camada híbrida e no adesivo no tempo de 24 horas e fraturas coesivas no cimento no tempo de 30 dias; no grupo III predominou as fraturas coesivas na camada híbrida nos tempos de 24 horas e 30 dias e finalmente para o grupo IV houve predominância de fraturas mistas, sendo coesivas no cimento, na camada híbrida e no adesivo para os tempos de 24 horas e 30 dias. As análises morfológicas das áreas da união não revelaram a formação da camada híbrida para o cimento auto-adesivo Rely X Unicem, enquanto que os cimentos dual Rely X ARC/Single Bond 2 e autopolimerizável C&B Cement/All Bond 2 apresentaram camada híbrida com semelhante morfologia / Abstract: The aim of this study was to evaluate bond strength and the interface morphology between human dentin and resin cements. Oclusal surfaces of 20 third molars were removed and middle dentin was finished with #600 grit SiC. Circular, 2mm thick, indirect composite resin restorations (Sinfony) were made and sandblasted with aluminum oxide and then silanized. Teeth were divided in five groups according to luting technique: Group I ¿ Rely X Unicem/ light-cure; Group II ¿ Rely X ARC/ Single Bond 2/ light-cure; Group III ¿ C& B Cement/ All Bond 2; Group IV ¿ Rely X ARC/ Single Bond 2/ self-cure and Group V ¿ Rely X Unicem/ self-cure. After cementation the teeth/restoration samples were stored in distilled water for 24 hours at 37oC and cut into beam specimens with 0.8±1.0mm2 cross-sections and microtensile tested after 24 and 30 days using a universal testing machine. Fracture patterns were observed and classified by SEM. Results were submitted to ANOVA and Tukey¿s Test to compare groups and pared t-test to compare the storage times of 24hours and 30 days (p<0,05). To analyze interface morphology, 2mm thick flat dentin discs were obtained. After cementation according to the experimental groups the dentin discs were cut vertically and embedded in epoxy resin for the procedures of finishing and gold-sputter. Results revealed that groups III, IV and V presented statistically significant bond strength increase after a storage period of 30 days. Light-cure groups revealed greater bond strength values at the storage times of 24hours and 30 days. SEM fracture pattern evaluation revealed a predominance of cohesive fractures in cement for groups I and V at 24 hours and 30 days. Group II revealed a higher frequency of mixed fractures which were cohesive in cement, hybrid layer and adhesive at 24 hours and cohesive in cement at 30 days. Group III presented more cohesive fractures at the hybrid layer at 24 hours and 30 days while group IV showed a predominance of mixed fractures which were cohesive in cement, hybrid layer and adhesive at 24hours and 30 days. While the morphologic analysis of bonded areas for the self-adhesive cement Rely X Unicem did not reveal the formation of a hybrid layer, the dual-cure cement Rely X ARC/Single Bond 2 and the self-cure cement C&B Cement/All Bond 2 presented hybrid layers with similar morphology / Doutorado / Materiais Dentarios
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288164 |
| Date | 06 February 2008 |
| Creators | Vaz, Ricardo Rodrigues |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954-, Pegoraro, Luiz Fernando, Junior, Walter Gomes Miranda, Bottino, Marco Antonio, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 80f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds