Orientador: Regina Maria Puppin Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odongologia / Made available in DSpace on 2018-08-20T02:53:07Z (GMT). No. of bitstreams: 1
Banzi_EfaniCarolinedeFreitas_D.pdf: 4070874 bytes, checksum: 96d960b77465f1ae2b52d04aed993c83 (MD5)
Previous issue date: 2012 / Resumo: Esta tese apresenta três capítulos. O Capítulo 1 avaliou o efeito dos sistemas adesivos, Clearfil SE Protect (primer com monômero antibacteriano) (CP), Clearfil SE Bond (CB) e Adper Single Bond 2 (SB) e do digluconato de clorexidina 2% (CHX) sobre Streptococcus mutans. Bactérias viáveis foram mensuradas depois que, fatias de dentina contaminadas com S. mutans foram limpas ou não com CHX e tratadas com os sistemas adesivos, e depois que discos de sistemas adesivos foram incubados em suspensão bacteriana. Para a contagem bacteriana usou-se teste de Friedman, ANOVA-R e teste t (LSD), para o tamanho dos halos de inibição foi utilizado Kruskal-Wallis e teste t (p<0.05). CP quando comparado com o CB mostrou maior efeito antibacteriano após 60 min de contato com as bactérias. A CHX não aumentou o efeito antibacteriano dos sistemas adesivos. O CP mostrou efeito inibidor no crescimento de S. mutans na superfície do ágar. Conclui-se a CHX não teve efeito no S. mutans antes da aplicação dos sistemas adesivos. CP exibiu considerável atividade antibacteriana e pode ser útil para reduzir bactérias cariogênicas. O Capítulo 2 avaliou a atividade antibacteriana do CP e do CB contra Streptococcus, Actinomyces e Lactobacillus. Discos dos sistemas adesivos foram mantidos em contato com 150 ?L de suspensões bacterianas de uma espécie ou misto de bactérias por 15, 30 e 60 minutos. A atividade metabólica foi determinada usando ensaio colorimétrico XTT e a viabilidade bacteriana foi mensurada usando os ensaios MTT e Live/Dead. Os resultados foram submetidos à ANOVA e ao teste f de Scheffe (p<0.05). O CP apresentou efeito bactericida na suspensão bacteriana comparado ao CB e ao Controle (suspensão bacteriana sem tratamento) nos três ensaios. Para a suspensão com três espécies bacterianas o CP agiu após 60 minutos de contato. Conclui-se que o CP é bactericida após a polimerização contra bactérias cariogênicas. O Capítulo 3 avaliou o efeito do CP, CB e CHX na resistência da união (RU) e na degradação da interface resina/dentina após ciclagem termomecânica (TM). A RU, degradação adesiva, adaptação marginal e nanoinfiltração foram avaliadas após os espécimes de dentina desmineralizada serem limpos ou não com CHX, tratados com CP ou CB e receberem ou não ciclagem TM (500 ciclos térmicos e 100.000 ciclos mecânicos). Os resultados foram submetidos a ANOVA três fatores e ao teste de Tukey (5%). A análise do modo de fratura, a porcentagem de fenda marginal e a nanoinfiltração foram analisados de forma descritiva. Não houve diferença estatística para a RU entre os grupos com e sem TM, contudo, a aplicação de CHX aumentou a RU para os espécimes TM e houve predomínio de falha mista. Fenda marginal foi observada em todos os espécimes, mas a porcentagem de fenda foi maior nos espécimes do grupo TM. Todos os grupos mostraram nanoinfiltração na interface adesiva e aumento do depósito de prata foi observado após a ciclagem termomecânica. Conclui-se que o sistema adesivo não afetou a RU. A CHX aumentou a RU e teve um efeito positivo na prevenção da nanoinfiltração após a ciclagem / Abstract: This Thesis present three chapters. The Chapter 1 evaluated the effect of bonding systems Clearfil SE Protect (primer with antibacterial monomer) (CP), Clearfil SE Bond (CB) e Adper Single Bond 2 (SB) and 2% digluconate chlorhexidine (CHX) on Streptococcus mutans. Viable bacteria were verified after that dentine slices contaminated with S. mutans were cleaned or not with CHX and treated with adhesive systems, and after that adhesive systems discs were incubated in bacterial suspension. The bacterial counts were analyzed using the Friedman test, ANOVA-R and t test (LSD), and the inhibitory zones were analyzed using the Kruskal-Wallis and t test (LSD) (p<0.05). CP when comparing with CB showed higher antibacterial effect after 60 min of bacterial contact. CHX did not improve the antibacterial effect of the bonding systems. Cured CP specimens showed an inhibitory effect on the growth of S. mutans on the agar surface. It was concluded that treatment of the dentin surface with CHX did not have an effect on S. mutans before applying bonding systems. CP exhibited considerable antibacterial activity and may be useful for reducing cariogenic bacteria. The Chapter 2 investigated the antibacterial effect of CP and CB against Streptococcus. Actinomyces and Lactobacillus. Discs of adhesive systems were kept in contact with 150 ?L of single or mixed bacterial suspension by 15, 30 and 60 minutes. The metabolic activity was determined by XTT assay and the viability bacterial by MTT and Live/Dead assay. Results were submitted to ANOVA and Scheffe's f-test (p<0.05). The CP showed bactericidal effect on the bacterial suspension compared with CB and buffer control (bacterial suspension without treatment), in all three assays. To three mixed bacterial suspensions the CP presented effect after 60 contact with bacteria. It was concluded that the CP was bactericidal after cured against cariogenic bacteria. The Chapter 3 evaluated the effect of CP, CB and CHX on the bond strength (BS) and bonding degradation of the resin/dentin interface after thermomechanical cycling (TM). The BS, bonding degradation, marginal adaptation, nanoleakage were analyzed after the specimens demineralized dentin were cleaned or not with CHX, treated with CP or CB and received or not TM (500 cycles thermal/100.000 cycles mechanical). Data were submitted to three-way ANOVA and Tukey's test (5%). The failure mode, percentage of gap marginal and the nanoleakage were evaluated descripitivelly. There was no difference significance to bond strength among group that received or not TM; however, the CHX maintained the bond strength for specimens of TM group and showed mixed failure for theses groups. Marginal gap was observed on all specimens, but to TM group the percentage of marginal gap was increased. All groups showed nanoleakage at the resin/dentin interfaces and an increase in silver deposition could be notice after thermomechanical cycling. It was concluded that adhesive system did not affect the bond strength. CHX increased the bond strength and had a positive effect to prevent nanoleakage after thermomechanical cycling / Doutorado / Odontopediatria / Doutor em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288586 |
| Date | 20 August 2018 |
| Creators | Banzi, Éfani Caroline de Freitas, 1981- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Myaki, Silvio Issao, Giro, Elisa Maria Aparecida, Pascon, Fernanda Miori, Najufel, Fabiana Scarparo |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 86 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds