Previous issue date: 2015 / Resumo: Este estudo in vitro avaliou a influência do pré-aquecimento na resistência de união de três agentes utilizados para a cimentação de pinos de fibra de vidro Reforpost nº 2. Para tal propósito, foram utilizadas 42 raízes de pré-molares humanos previamente extraídos e com tratamento endodôntico realizado e foram divididos, aleatoriamente, em 6 grupos (n=7) de acordo com o agente de fixação (um cimento resinoso dual Rely X ARC; um cimento autoadesivo Rely X U200; e uma resina composta de baixa viscosidade SureFil SDR flow) e temperatura de pré-aquecimento (23ºC; 54ºC). Todos os agentes de cimentação foram fotoativados através de uma fonte de luz LED com irradiância de 1100 mW/cm² durante 40 segundos. As raízes foram armazenadas em água destilada à 37ºC por sete dias e foram cortadas em fatias com espessura de 1,0 mm cada, os quais foram divididos de acordo com o terço do canal radicular (cervical; médio; apical). Em seguida, as amostras foram submetidas ao teste de resistência ao cisalhamento por extrusão para a mensuração em cada terço do canal radicular. Os dados foram submetidos à ANOVA 3 critérios com parcelas subdivididas e teste de Tukey (? = 0,05). Foram encontradas diferenças significativas entre os três cimentos resinosos. (P < 0,0017); no entanto não foram encontradas diferenças entre os grupos não aquecidos e os grupos pré-aquecidos, diferentes regiões da raiz ou para qualquer interação entre os fatores (p > 0,05). Os grupos cimentados com o cimento resinoso Rely X ARC apresentou maiores resultados de resistência de união do que os grupos cimentados com a resina de baixa viscosidade SureFil SDR flow. O cimento autoadesivo Rely X U200 obteve resistência de união intermediária, sem diferença estatística para RelyX ARC ou SureFil SDR flow. Assim, conclui-se que, a utilização de cimento dual convencional pode ser indicada para cimentação de pinos de fibra de vidro e que o pré-aquecimento de cimentos resinosos não é efetivo para o aumento da resistência de união de pinos pré-fabricados / Abstract: This in vitro study investigated the influence of pre-heating on the bond strength of three agents used for cementing fiber posts Reforpost # 2. For that, forty-two human premolars roots with endodontic treatment performed were randomly divided into 6 groups (n = 7), according with the luting agent (a dual resin cement Rely X ARC; a self-adhesive cement Rely X U200; and a flowable composite SureFil SDR flow) and the pre-heating temperature (23° C; 54° C). All luting agents were light-cured with a LED unit ¿ 1,100 mW/cm² for 40 seconds. The roots were stored in distilled water at 37° C for seven days and after that, the roots were cut into slices of 1.0 mm thickness each, which were divided according to the third of the root canal (cervical; middle; apical). Then the specimens were submitted to push out test to measure the bond strength in each third of the root canal. Data were submitted to three-way split-spot ANOVA and Tukey's test (? = 0.05). Significant differences were found among the three luting agent studied (p < 0.0017); however, no difference was found among the pre-heating temperature, root segments or for any interaction between the factors (p > 0.05). Groups luted with resin cement Rely X ARC showed significant higher retentive strength than flowabe composite SureFil SDR flow. Rely X U200 showed intermediary retentive strength means, without statistical difference for Rely X ARC or SureFil SDR flow. Thus, it is concluded that the use of conventional dual cement should be indicated to luting fiber posts and the resin cement pre-heating is not effective to increase the retentive strength of fiber post / Doutorado / Dentística / Doutora em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288864 |
| Date | 27 August 2018 |
| Creators | Hernandes da Fonseca, Natália Maria Aparecida, 1986- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Aguiar, Flávio Henrique Baggio, 1977-, Neto, Laurindo Borelli, Barros, Tarley Eloy Pessoa de, Lima, Débora Alves Nunes Leite, Paulillo, Luis Alexandre Maffei Sartini |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 45 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds