Orientador: Flávio Henrique Baggio Aguiar / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T21:16:27Z (GMT). No. of bitstreams: 1
Mainardi_MariadoCarmoAguiarJordao_M.pdf: 989642 bytes, checksum: dd3fc3a3b18282f2bf45daefa47de5de (MD5)
Previous issue date: 2013 / Resumo: O objetivo neste estudo foi avaliar o grau de conversão (GC) e microdureza (KHN) de um cimento resinoso dual utilizado para a fixação de pinos de fibra de vidro. Para isso, foram utilizadas 45 raízes (n=5) de incisivos bovinos, as quais foram submetidas ao tratamento endodôntico e divididas em 8 grupos experimentais e um controle. Após o tratamento endodôntico, as raízes foram desobturadas e pinos de fibra de vidro White Post DC nº 3 foram cimentados, com o cimento resinoso dual RelyX ARC (3M-ESPE). A seguir, a fotoativação foi realizada com o aparelho LED (Valo-Ultradent) em quatro diferentes densidades de energia (7, 14, 20 ou 28 J/cm²) e dois diferentes tempos de espera (0 ou 2 minutos). O grupo controle não foi fotoativado. Após a cimentação as raízes com os pinos cimentados foram armazenadas em água destilada a 37º C durante 15 dias. Após esse período os valores de grau de conversão e microdureza Knoop foram coletados em três diferentes terços do canal radicular (Cervical, Médio e Apical). Os dados foram submetidos à análise de variância três fatores com parcelas subdivididas (ANOVA) e teste de Tukey. Comparações com o grupo controle foram realizadas pelo teste de Dunnett. Através dos resultados obtidos para grau de conversão, pode-se observar que o terço Cervical apresentou os maiores resultados, estatisticamente diferente dos demais terços, para todas as condições experimentais. O grau de conversão para o tempo de espera de 2 minutos foi estatisticamente maior do que aquele apresentado pelo tempo imediato. A densidade de energia 28 J/cm² apresentou os maiores valores de grau de conversão, com diferença estatística significante das demais densidades de energia. Para os valores de microdureza, não houve diferenças estatísticas em relação aos tempos de espera. Dentro dos terços Cervical e Apical, não houve diferenças significantes em relação às densidades de energia. No terço Médio, a fotoativação com 14 J/cm² apresentou os maiores valores de microdureza, enquanto 28 J/cm² resultou nos menores. O terço Apical não diferiu estatisticamente em relação ao mesmo terço do grupo controle. Pelos resultados obtidos pode-se concluir que o grau de conversão foi influenciado pelas densidades de energia e tempos de espera para a fotoativação, assim como pelo terço do canal radicular. Os valores de microdureza não foram influenciados pelo tempo de espera para a fotoativação, e as diferentes densidades de energia apresentaram comportamento semelhante nos terços Cervical e Apical / Abstract: The aim of this study was to evaluate the degree of conversion and microhardness of dual-cured resin cement used for cementation of fiber posts. Forty-five roots of bovine incisors were used for this purpose. These roots were submitted to endodontic treatment and random assigned to 8 experimental groups and a control, all of them with n=5. After seven days, the fiber post White Post DC #3 was cemented with the dual-cured resin cement, RelyX ARC (3M-ESPE) in each root. Following this step, the light curing was performed with the 3ª generation LED device (Valo-Ultradent), with four different energy densities (7, 14, 20 or 28 J/cm²) and two different delay times (o or 2 minutes). The control group was not light-cured. After the cementation, the roots were stored in distilled water at 37º C for 15 days, and the degree of conversion an Knoop microhardness were obtained in three different root segments (Cervical, Medium and Apical). Data were submitted to three-way split-spot ANOVA and Tukey's test. Dunnett's test was used for comparisons with control. Results of degree of conversion showed that the Cervical root segment obtained higher values than the others, at all experimental conditions. The degree of conversion values for 2-minutes delay time were higher than 0-minute delay-time. The energy density of 28 J/cm² obtained the highest values, with significant differences from the others energy densities. For microhardness values there were not significant differences between the delay times. For the Cervical and Apical root segments, there were not statistical differences for the energy densities tested. The energy density of 14 J/cm² showed the higher values of microhardness at the Medium root segment, while the 28 J/cm², showed the lowest. The Apical root segment obtained similar microhardness values from the same third at the control. In conclusion, the degree of conversion was influenced by the energy densities and delay times, as well as the root segment. The microhadness was not affected by the delay time at all conditions, and the energy densities showed similar behavior at Cervical and Apical root segments / Mestrado / Dentística / Mestra em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288866 |
| Date | 22 August 2018 |
| Creators | Mainardi, Maria do Carmo Aguiar Jordão, 1981- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Aguiar, Flávio Henrique Baggio, 1977-, França, Fabiana Mantovani Gomes, Paulillo, Luis Alexandre Maffei Sartini |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 41 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds