Orientador: Francisco Jose Souza Filho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-14T06:25:48Z (GMT). No. of bitstreams: 1
Berger_CarlosRoberto_D.pdf: 7347210 bytes, checksum: 564e46ae66009c800a919cd31561e9b8 (MD5)
Previous issue date: 2009 / Resumo: Esse estudo avaliou a composição química da parte inorgânica e a presença de formaldeído em cimentos endodônticos indicados para obturação do sistema de canais radiculares. Sete cimentos endodônticos foram escolhidos: quatro a base de óxido de zinco e eugenol (Targer Canal Sealer - Konne; Endo Fill - Dentsply; Endométhasone N - Septodont e; Pulp Canal Sealer EWT - Kerr); dois a base de agregado trióxido mineral (MTA) (Endo CPM Sealer - EGEO Dental e Obtura - Ângelus) e; um a base de resina/hidróxido de cálcio (Sealer 26, Dentsply). Todos os materiais foram manipulados de acordo com as recomendações de cada um dos fabricantes e inseridos em um porta-amostra de 5 cm de diâmetro e 0,5 cm de altura. Após tomar presa foram analisados através de dois métodos: Difratometria de Raios X, para a análise da parte inorgânica dacomposição química dos cimentos e Cromatografia, para análise da presença de formaldeído. Os resultados demonstraram que: todos os cimentos a base de óxido de zinco e eugenol apresentam óxido de zinco em altas concentrações. Os cimentos Target Canal Sealer e Endo fill, apresentam também na sua composição sulfato de bário e carbonato de bismuto. O cimento Endométhasone N apresentou apenas sulfato de bário e o Pulp Canal Sealer, prata metálica. Já o cimento a base de resina/hidróxido de cálcio, Sealer 26, apresenta óxido de bismuto, hidróxido de cálcio, dióxido de titânio e óxido de ferro. Os dois cimentos a base de MTA testados, Endo CPM Sealer e Obtura, apresentaram basicamente, silicato de cálcio. Componentes tais como: sulfato de bário e carbonato de cálcio foram encontrados no Endo CPM Sealer e hidróxido de cálcio e silicato de magnésio foram encontrados no Obtura. Em relação à presença de formaldeído, todos os materiais testados apresentaram formaldeído após a manipulação. Com base nestes dados, pode-se concluir que: 1) Não houve uma coincidência entre a composição divulgada pelo fabricante e a observada experimentalmente através da Difratometria de Raios X. Exceção a este são os cimentos a base de MTA; 2) apesar de nenhum fabricante indicar a presença de formaldeído na composição do material, este composto foi verificado em todos os cimentos testados, após manipulação. / Abstract: This study evaluated chemical composition (inorganic) and formaldehyde presence in root-canal sealers. Seven root-canal sealers were chosen: four based-zinc-oxide-eugenol (ZOE) (Targer Canal Sealer, Konne; Endo Fill, Dentsply; Endométhasone N, Septodont and; Pulp Canal Sealer, Kerr); two based-mineral trioxide aggregate (MTA) (Endo CPM Sealer, EGEO Dental and Obtura, Ângelus) and; one based-resin/calcium hydroxide (Sealer 26, Dentsply). All materials were mixed according to the manufacturer's instructions and inserted in one matrix (5 cm diameter and 0.5 cm thickness. X-Ray Powder Diffraction and Chromatography was performed after freshly mixed, for chemical composition and presence of formaldehyde, respectively. The results showed that: all ZOE materials presented higher concentrations of zinc-oxide. Target Canal Sealer and Endo fill based-OZE cements, showed barium sulfate and bismuth carbonate in the composition. Endométhasone N cement presented only barium sulfate and Pulp Canal Sealer, metal silver. Bismuth oxide, calcium hydroxide, titanium dioxide and iron oxide were showed in the based-resin/calcium hydroxide (Sealer 26). Both of MTA cements tested, Endo CPM Sealer and Obtura, presented calcium silicate. However, barium sulfate and calcium carbonate was found in the Endo CPM Sealer and magnesium silicate and calcium hydroxide in the Obtura. Regarding to the formaldehyde, all root-canal sealers tested showed this substance after took mixed. It was concluded that: 1) there was a great difference among present results and manufacturer's composition for almost all materials. This was notobserved for MTA root-canal sealers; 2) although no manufacturer has indicated the formaldehyde presence in their material composition, this component was verified in all materials tested. / Doutorado / Endodontia / Doutor em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288973 |
| Date | 14 August 2018 |
| Creators | Berger, Carlos Roberto |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Souza Filho, Francisco José de, 1950-2014, Sydney, Gilson Blitzzckow, Loguercio, Alessandro Dourado, Gomes, Brenda Paula Figueiredo de Almeida, Ferraz, Caio Cezar Randi |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 137 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0042 seconds