Orientador: Lourenço Correr Sobrinho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T01:34:04Z (GMT). No. of bitstreams: 1
Paes_PaulaNunesGuimaraes_M.pdf: 8634173 bytes, checksum: 841ceeadf71622e4274b862220cdb566 (MD5)
Previous issue date: 2009 / Resumo: O objetivo deste estudo foi avaliar o efeito dos métodos de ativação e da fadiga mecânica sobre a resistência à tração diametral de cimentos resinosos duais. Pastas base e ativadora do RelyX ARC, Enforce, Nexus 2 e RelyX UNICEM foram manipuladas e inseridas em matrizes cilíndricas de silicona de adição (4 x 2 mm) e distribuídas em grupos de acordo com a técnica de ativação em: 1- Sem fotoativação (ativação química); 2- Fotoativação direta (ativação Dual); 3- Fotoativação através da cerâmica. Após armazenamento por 24 horas em água destilada a 37ºC, metade das amostras de cada grupo (n=10) foram submetidos a 30.000 ciclos mecânicos, com freqüência de 1 Hz e carga de 12 N. As amostras não cicladas permaneceram armazenadas em água destilada em estufa a 37ºC por 32 h após a manipulação, para que fossem testadas com o mesmo intervalo
de tempo que as amostras cicladas. Em seguida, todas as amostras foram submetidas ao ensaio de Resistência à Tração Diametral (RTD) em máquina universal de ensaios INSTRON, com velocidade de 0,5 mm/min. Os dados de RTD (MPa) para os modos de ativação química, dual indireta e dual direta foram submetidos à análise de Variância e ao teste de Tukey (5%) e mostraram que apenas os fatores modo de ativação e cimento apresentaram interação
significativa. O fator ciclagem mecânica e a interação tripla não obtiveram interação significativa. Os valores da interação dos fatores cimento e modos de ativação química, dual indireta e dual direta respectivamente foram: RelyX ARC (49,68 ± 8,42; 63,43 ± 6,92 e 55,12 ± 5,16), Enforce (49,12 ± 3,89; 56,96 ± 6,45 e 56,42 ± 8,88), RelyX ARC (28,12 ± 11,21; 40,10 ± 4,39 e 37,44 ± 6,49) e Nexus 2 (61,89 ± 11,21; 62,56 ± 10,93 e 59,26 ± 9,47). A análise dos resultados após o
teste de Tukey mostrou que o cimento Nexus 2 não apresentou aumento nos valores de RTD quando ativado pela luz em relação à polimerização química. Os demais cimentos apresentaram valores maiores quando fotoativados de forma direta ou indireta, em relação aos valores alcançados pelo modo de polimerização química, com exceção do cimento RelyX ARC que obteve os mesmos valores quando ativado de forma dual direta e polimerizado quimicamente. A interposição
do disco de cerâmica durante a fotoativacão alterou os valores de resistência à tração diametral apenas para o cimento RelyX ARC. A ciclagem mecânica não afetou a resistência à tração diametral de nenhum cimento resinoso dual avaliado e a composição de cada cimento resinoso dual, assim como o seu modo de ativação, foram determinantes para a obtenção da resistência à tração diametral dos mesmos. / Abstract: The aim of this study was to evaluate the effect of the activation methods and the mechanical fatigue on diametral tensile strength of dual resin cements. Base and catalyst pastes of the cements RelyX ARC, Enforce, Nexus 2 and RelyX UNICEM were mixed and inserted into cylindrical silicon moulds (4 x 2 mm) and divided in groups according to their activation methods: 1) without photoactivation (chemical activation); 2) direct curing (dual ativation); 3) light activation through porcelain disk. After being stored for 24 hours in distillated water at 37ºC, half of the samples of each group (n=10) were subjected to 30,000 mechanical cycles at 1 Hz frequency and 12 N load. The samples not cycled remained in distillated water at 37ºC for 32 h after the mixing, so they were tested with the same time that the other fatigued samples did. Then, the samples were
subjected to Diametral Tensile Strength (DTS) in Instron universal machine with 0,5 mm/min speed. The data of the Diametral Tensile Strength (MPa) obtained for each cement in chemical, indirect dual and direct dual modes of activation were submeted to three-way analysis of variance and Turkey's Student Range Test (5%) and showed that only the activation methods and the cement type presented significant difference. Mechanical fatigue and triple factors interation didn't present
significant difference. The data of the cement factor with chemical activation, indirect curing and direct curing was respectively: RelyX ARC (49.68 ± 8.42; 63.43 ± 6.92 e 55.12 ± 5.16), Enforce (49.12 ± 3.89; 56.96 ± 6.45 and 56.42 ± 8.88), RelyX ARC (28.12 ± 11.21; 40.10 ± 4.39 and 37.44 ± 6.49) and Nexus 2 (61.89 ± 11.21; 62.56 ± 10.93 and 59.26 ± 9.47). After Turkey's test, the data showed that the cement Nexus 2 didn't present increase in the DTS values when it was light
actived comparing to chemical curing. The others cement presented higher values when directly or indirectly photoactivated compared with the values obtained with chemical activation mode. The exception was the RelyX ARC cement that obtained the same data when it was direct cured and chemical activated. The interposition of porcelain disk during the photoactivation did alter the DTS values only for the RelyX ARC cement. However, the mechanical fatigue didn't alter the DTS values of any dual resin cement tested. Each dual cement composition, as their activation
mode, was fundamental in order to obtain its DTS values. / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289569 |
| Date | 02 May 2009 |
| Creators | Paes, Paula Nunes Guimarães |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Correr Sobrinho, Lourenço, 1960-, Filho, Helio Rodrigues Sampaio, Puppin-Rontani, Regina Maria |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 71 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds