Orientador: Luis Roberto Marcondes Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T21:20:40Z (GMT). No. of bitstreams: 1
Leite_ThatianadeVicente_M.pdf: 962489 bytes, checksum: 384dca92c91450403a7ee6a9653d3bef (MD5)
Previous issue date: 2013 / Resumo: O objetivo deste trabalho foi avaliar, in vitro, a resistência de união (push-out) regional (terços cervical, médio e apical) de pinos de fibra de vidro (Reforpost #3, Ângelus Indústria de Produtos Odontológicos S/A, Londrina, PR) fixados com cimentos resinosos experimentais foto-ativados, contendo diferentes concentrações do sal hexafluorfosfato de difeniliodônio (DFI), variando as aminas terciárias entre EDAB e DMAEMA, e compará-los a um cimento resinoso disponível no mercado em sua versão dual e foto-ativável. Foram utilizadas 80 raízes de incisivos inferiores bovinos com 15 mm de comprimento e diâmetro do canal máximo de 2 mm, as quais foram divididas em 8 grupos experimentais (n = 10). Os grupos experimentais são descritos a seguir: G1 - cimento resinoso experimental, sem adição do sal DFI, contendo 2 mol % de EDAB; G2 - cimento resinoso experimental, com adição de 0,5 mol % do sal DFI, contendo 2 mol % de EDAB; G3 - cimento resinoso experimental, com adição de 1 mol % do sal DPI, contendo 2 mol % de EDAB; G4 - cimento resinoso experimental, sem adição do sal DFI, contendo 2 mol % de DMAEMA; G5 - cimento resinoso experimental, com adição de 0,5 mol % de DFI, contendo 2 mol % de DMAEMA; G6 - cimento resinoso experimental, com adição de 1 mol % de DFI, contendo 2 mol % de DMAEMA; G7 - cimento resinoso comercial Variolink II, versão foto-ativável, utilizando apensas a pasta base; G8 - cimento resinoso comercial Variolink II (Ivoclar-Vivadent), versão dualmente ativável, utilizando as pastas base e catalisadora. Para todos os grupos, o protocolo adesivo utilizado foi condicionamento ácido, seguido pela aplicação do primer e bond Scotchbond Multipurpose (3M ESPE). Após a cimentação, o teste de resistência de união push-out foi realizado a uma velocidade de 1 mm/min, utilizando uma célula de carga de 200 N e os valores expressos em MPa. A análise do padrão de fratura foi realizada em lupa estereoscópica (LEICA MZ75 50X). Os dados coletados foram submetidos à Análise de Variância a um critério com parcelas subdivididas e teste de Tukey (?=0.05). Os resultados obtidos demonstraram que não houve diferença estatística entre o comportamento dos cimentos devido à influência das diferentes aminas; os cimentos experimentais resinosos que continham o sal DFI (grupos 2,3,5 e 6) apresentaram os maiores valores de resistência de união para todos os terços estudados (cervical, médio e apical), sendo estes estatisticamente semelhantes ao cimento resinoso comercial Variolink II dual (grupo 8). Os menores valores apresentados foram para os cimentos que não continham o sal DFI (grupos 1 e 4) e para o cimento resinoso comercial Variolink II foto-ativável (grupo 7), sendo estes estatisticamente semelhantes no terço apical. O cimento resinoso experimental foto-ativável contendo sal de DFI se mostrou capaz para a cimentação de pinos de fibra de vidro, sendo estatisticamente semelhantes ao cimento resinoso comercial Variolink II Dual, e superiores ao mesmo cimento em sua versão fotoativável. A região apical demonstrou para todos os grupos os menores valores de resistência de união. O tipo de amina terciária e a concentração do sal de DFI (0,5 e 1 mol %) não influenciaram a resistência de união de pinos de fibra de vidro à dentina radicular / Abstract: The aim of this study was to evaluate, in vitro, the bond strength (push-out) of fiber posts fixed with experimental photo-activated resin cements with the addition of different concentrations of hexafluorophosphate dipheniliodonium salt (DFI), also varies between tertiary amines EDAB and DMAEMA in cementation of fiber posts, and compare them to a resin cement available in the market in its dual and photo-activatable version. A total of 80 bovine incisors roots of similar dimensions were used, which were divided into eight experimental groups (n = 10). Experimental groups are described below: G1 - experimental resin cement without addition of DFI salt, containing 2 mol% EDAB; G2 - experimental resin cement, with addition of 0.5 mol% of DFI salt containing 2 mol % of EDAB; G3 - experimental resin cement with addition of 1 mol% of DFI salt, containing 2 mol% EDAB; G4 - experimental resin cement without addition of DFI salt, containing 2 mol% DMAEMA; G5 - experimental resin cement, with addition of 0.5 mol% DFI salt, containing 2 mol% DMAEMA; G6 - experimental resin cement with the addition of 1 mol% DFI salt, containing 2 mol% DMAEMA; G7 - commercial resin cement Variolink II, photo-activatable version, using the base paste; G8 - commercial resin cement Variolink II, version dually activatable, using the base and catalyst pastes. For all groups, the adhesive protocol used was, etching, followed by application of primer and bond Scotchbond Multipurpose. After cementation, the bond strength test push-out was conducted at a speed of 1 mm / min, using a load cell of 200 N and the values expressed in MPa. The pattern of fractures was performed by stereoscopy magnifier (LEICA MZ75 50X). The collected data were subjected to ANOVA for a split-plot criterion and the Tukey test (? = 0.05). The results showed that there was no statistical difference in the behavior of cements due to influences of the different amines; experimental resin cements containing salt DFI (groups 2,3,5 and 6) showed the highest bond strength for all the studied thirds (cervical, middle and apical), which are statistically similar to the commercial resin cement Variolink II Dual (group 8). The lowest values were submitted to the cements containing no DFI salt (groups 1 and 4) and the commercial resin cement Variolink II photo-activable (group 7), which were statistically similar in the apical third. The experimental resin cements containing DFI salt are capable for fiber glass posts cementation, being statistically similar to the commercial resin cement Variolink II Dual, and even above the cement in the version photo-activable. The variation of tertiary amines did not influence the results of bond strength and there was no statistically difference between the concentrations 0.5 mol% and 1 mol% of DFI salt / Mestrado / Materiais Dentarios / Mestra em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289698 |
| Date | 04 May 2013 |
| Creators | Leite, Thatiana de Vicente, 1988- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Martins, Luís Roberto Marcondes, 1960-, Atta, Maria Teresa, Baron, Giselle Maria Marchi |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 47 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds