Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T12:43:43Z (GMT). No. of bitstreams: 1
Goncalves_LucianodeSouza_D.pdf: 1422797 bytes, checksum: d08f8aa4d184071d3c75843275b3cdea (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar a influência da incorporação de um sal de hexafluorofosfato de difeniliodônio (DFI) nas propriedades de um cimento resinoso experimental. Uma composição à base de monômeros Bis-GMA e TEGDMA, na proporção de 1:1 mol%, foi obtida e a ela adicionadas concentrações de 0 (controle), 0,25, 0,5, 1 ou 2 mol% de DFI, definindo 5 formulações de cimentos resinosos experimentais. O sistema fotoiniciador dos materiais foi composto por 1 mol% de canforoquinona e 2 mol% de metacrilato de dimetilaminoetil. Como inibidor foi usado 0,1 mol% de hidroxibutil tolueno e 60% em peso de partículas silanizadas de vidro de bário-alumínio-silicato foram incorporadas como carga inorgânica. Depois da preparação dos cimentos foram realizados os seguintes ensaios: 1) Cinética da polimerização em tempo real em espectroscopia infravermelha, indicando também o grau de conversão dos cimentos. 2) Resistência à flexão de três pontos e módulo de elasticidade, definido pelo monitoramento do ensaio com software específico. 3) Sorção e solubilidade em água destilada (21 dias). 4) Tensão da contração de polimerização mensurada em máquina de ensaios mecânicos associada a extensômetro. 5) Dureza Knoop avaliada na base e no topo de corpos-de-prova fotoativados diretamente ou através de discos de cerâmica com 3 espessuras diferentes. A análise estatística foi realizada com significância de 5%. Os resultados mostraram que a adição do DFI influenciou as propriedades em todos os ensaios realizados. As formulações de cimentos com DFI apresentaram aumento na cinética da reação, no grau de conversão e na dureza Knoop. Houve aumento significativo na resistência à flexão e no módulo de elasticidade e redução nos valores de sorção de água e perda de massa por solubilidade. Na maioria dos grupos contendo DFI, os valores de tensão da contração de polimerização foram similares ao grupo controle, exceto o grupo 4 com 1 mol% de DFI que apresentou aumento na tensão gerada pela polimerização. Com base nos resultados obtidos foi possível concluir que a adição do DFI influenciou positivamente as propriedades dos cimentos resinosos experimentais e a concentração de 0,5 mol% parece ser a mais conveniente para a formulação desses cimentos resinosos estudados. / Abstract: The aim of this study was to evaluate the effect an onium salt -diphenyliodonium hexafluorphosphate (DPI) - on selected properties of experimental resin cement. A model Bis-GMA/TEGDMA comonomer blend (1:1 molar ratio) was obtained and DPI added at concentrations of 0 (control), 0.25, 0.5, 1 or 2 mol%, resulting in five experimental resin cements. The photoinitiator system was composed by 1 mol% of camphorquinone and 2 mol% of dimethylaminoethil methacrylate. 0.1mol% of hydroxyl butyl toluene was used as a inhibitor and the cements were loaded with a 60% mass fraction of silanated Ba-AI-Si glass fillers. The following analyzes were carried out: 1) real-time polymerization kinetics using near-infrared spectroscopy, 2) flexural strength and flexural modulus using a three-point beinding test, 3) water sorption and solubility after immersion for 21 days, 4) polymerization stress on a mechanical testing machine, and 5) Knoop hardness on the top and bottom surfaces of cement discs light-activated through different ceramic thicknesses. Data were statistically analyzed (5%). The results showed the addition of DPI had influence on the resin cements for all analyses. DPI-containing materials showed improved polymerization kinetics and degree of conversion, as well as higher hardness. A significant increase in flexural strength and modulus, and decrease in water sorption/solubility was detected. Most of materials containing DPI showed polymerization stress values comparable to the control group, except for the material containing 1 mol% of DPI (G4), which yielded higher stress. Based on these results and within the limitations of the study, it was possible to conclude that the addition of DPI has positive influence on the properties of the experimental resin cement; the 0.5 mol% concentration seems to be the most appropriate and efficient for the formulation of these resin cements. / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290061 |
| Date | 17 August 2018 |
| Creators | Gonçalves, Luciano de Souza |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Borges, Luis Henrique, Vaz, Ricardo Rodrigues, Sinhoreti, Mário Alexandre Coelho, Correr Sobrinho, Lourenço |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 62 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds