Orientador: Antonio Carlos Pereira / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T16:12:35Z (GMT). No. of bitstreams: 1
Gomes_MariaJose_D.pdf: 4567266 bytes, checksum: b2011f19e433369366af4926c5f7afd5 (MD5)
Previous issue date: 2003 / Resumo: O objetivo deste estudo foi avaliar o % de volume mineral x mm do esmalte dental microabrasionado submetido a um modelo de ciclagem de pH, o qual simula o desafio cariogênico que ocorre na cavidade bucal. Cento e oito (108) blocos de esmalte obtidos de dentes com fluorose (TF2 ou TF3) foram selecionados (12 blocos por grupo) e submetidos a 9 tratamentos: Grupo I - Controle (sem tratamento); Grupo II - FFA (aplicação tópica de flúor fosfato acidulado 1,23%); Grupo III - FN (aplicação tópica de fluoreto de sódio neutro 2%); Grupo IV Opalustre® (microabrasão com o Opalustre® - microabrasivo composto por ácido clorídrico 6,6% e carboneto de silício); Grupo V ¿ Opalustre® + FFA (microabrasão com Opalustre® seguido da aplicação tópica de FFA 1,23%); Grupo VI Opalustre® + FN (microabrasão com Opalustre® seguido da aplicação tópica de FN 2%); Grupo VII - Ácido fosfórico (microabrasão com pasta de ácido fosfórico 37% em gel e pedra-pomes 1:1; Grupo VIII - Ácido fosfórico + FFA (microabrasão com pasta de ácido fosfórico 37% e pedra-pomes 1:1, seguido da aplicação tópica de FFA 1,23%); Grupo IX - Ácido fosfórico + FN (microabrasão com pasta de ácido fosfórico 37% em gel e pedra-pomes 1: 1, seguido da aplicação tópica de FN 2%). Após os tratamentos os blocos foram submetidos a um modelo de ciclagem de pH durante 7 dias, alternando períodos de desmineralização (3 horas, pH 4,3, Ca e PO4 mM, tampão acetato 0,075 M) e remineralização (21 horas, pH 7,0, Ca 1,5mM, PO4 0,9mM, KCI 0,015M, tampão TRIS 0,1 M). Após a ciclagem cada bloco foi seccionado ao meio com um corte longitudinal passando pelo centro da área teste e embutido em resina acrílica para análise da microdureza. A microdureza Knoop em secção longitudinal foi determinada, os valores transformados em % de volume mineral x mm para calculo da área da lesão de cárie. Foi realizada a análise de variância (ANOVA) e aplicado o teste de Tukey a 5%. Os resultados (média e desvio padrão) obtidos foram: Controle (562,94±24,4 a), FFA (300,38±34,59 b), FN (568,32 ±23,49 a), Opalustre® (304,43±100,68 b), Opalustre® + FFA (134,46± 44,76 c), Opalustre® + FN (244,75 ±66,53 b), Ácido fosfórico (582,90 ±44,39 a), Ácido fosfórico + FFA (65,87 ±22,22 d), Ácido fosfórico + FN (106,68±13,67 c) (p<O, O5). Estes resultados permitiram concluir que os dois sistemas microabrasivos empregados neste estudo diminuíram o % de volume mineral x m (DZ) do esmalte dental, quando este foi submetido a um modelo de ciclagem de pH. O sistema microabrasivo composto pela pasta de acido fosfórico a 37% mais pedra-pomes 1:1 seguido da aplicação tópica de FFA apresentou o melhor resultado em termos de limitação da perda mineral. A aplicação tópica de flluoretos foi um fator determinante na diminuição da perda mineral do esmalte microabrasionado, e nestas condições o FFA foi mais efetivo do que o FN / Abstract: a) The purpose of this study was to evaluate % of mineral caries lesion of microabraded enamel surfaces to demineralization using a pH cyling model, wich simulates the caries conducive environment of the oral cavity. Thus, 108 enamel blocks from teeth with fluorosis (TF2 ou TF3) were selected (12 blocks each group) and taken to 9 treatments: group I- Control (no treatment), group II - AFP (1.23% acid Fluoride Phosphate), group III - NF (2% Neutral Sodium Fluoride), group IV- Opalustre® (6.6% hydrochloric acid and silicon carbonite), group V Opalustre® + AFP (Opalustre® and 1.23% acid Fluoride Phosphate), group VI Opalustre® + NF (Opalustre® and 2% Neutral Sodium Fluoride), group VII - Phosphoric acid ( 37% phosphoric acid + pumice stone 1: 1), group VIII - Phosphoric acid + AFP ( 37% phosphoric acid + pumice stone 1:1 and 1.23% acid Fluoride Phosphate), group IX - Phosphoric acid + NF (37% phosphoric acid + pumice stone 1:1 and 2% Neutral Sodium Fluoride). After the treatment the blocks were taken to a pH cycling model for 7 days, alternating demineralization (3 hours, pH 4.3, Ca e PO4 mM, acetate buffer 0,075M) and remineralization (21 hours, pH 7.0, Ca 1,5mM, PO4 0.9mM, KCI 0.015M, TRIS buffer 0.1 M). Cross-sectional microhardness was determined and % of mineral in caries lesions (DZ) was calculated. A variance analysis (ANOVA) was performed and the Tukey test was applied in 5% of significance
leveI. The results (mean and ± sd) for: Control (562.94±24.4 a), AFP (300.38± 34.59 b), NF (568.32 ±23.49 a), Opalustre® (304.43±100.68 b), Opalustre® + AFP (134.46 ±44.76 c), Opalustre® + NF (244.75±66:53 b), Phosphoric acid (582.90±44.39 a), Phosphoric acid + AFP (65.87±22.22 d), Phosphoric acid + NF (106.68±13.67 c). Means followed by different letters are statistically significant (p<0.05). The results suggest that microabrasion systems limited the mineral loss of enamel when employed the pH cycling mode!. The microabrasion systems with 37% phosphoric acid and pumice stone 1:1 + AFP, 37% phosphoric acid and pumice stone 1:1 + NF showed the best result in limiting the mineral loss. The topic use of fluoride was very relevant to decrease the mineral loss and, in such conditions, the topic use of AFP was more effective than the NF / Doutorado / Cariologia / Doutor em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290336 |
| Date | 25 June 2003 |
| Creators | Gomes, Maria Jose |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Pereira, Antonio Carlos, 1967-, Mendes, Regina Ferraz, Mondelli, Jose, Hebling, Eduardo, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 138 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds