Tese (livre-docencia) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-24T00:14:49Z (GMT). No. of bitstreams: 1
Lovadino_JoseRoberto_LD.pdf: 3449328 bytes, checksum: b1898409a8af1238fb9ea2f6e7b3fce1 (MD5)
Previous issue date: 1997 / Resumo: Neste trabalho verificamos a rugosidade superficial, a suscetibilidade à deposição superficial de corante e a correlação entre estes dois fatores, quando a superfície de três compósitos (Adaptic, TPH e Herculite XRV) foram submetidas ao acabamento e polimento realizados com discos-de-lixa Sof-Lex (3M), Pontas Diamantadas (KG-Sorensen) e Pontas de Borracha Abrasiva (KG-Sorensen). Realizamos a análise da rugosidade da superfície com um rugosímetro (Praxis) e a suscetibilidade à deposição superficial de corante através de um método de espectrofotometria (Beckmam). Os resultados foram submetidos à análise estatística, não paramétrica, peio do teste de Kruskal-Wallis. Verificamos que os mesmos tratamentos produziram superfícies com valores de rugosidade (Ra) semelhantes para todos os materiais; que um mesmo material pode apresentar valores de Ra diferentes, quando submetidos aos diferentes tratamentos, e que o tratamento realizado com os discos-de-lixa Sof-Lex apresentou os menores valores de Ra e o realizado com Pontas Diamantadas, os piores. Também verificamos que os diferentes compósitos podem apresentar suscetibilidade semelhante à deposição superficial de corante, independentemente do tratamento utilizado; que os diferentes tratamentos empregados, num mesmo compósito, podem produzir superfícies com diferentes suscetibilidades e que o tratamento realizado com discos-de-lixa Sof-Lex produziram superfícies menos suscetíveis. Não foi verificada uma correlação confiável entre os valores de Ra e a suscetibilidade à deposição superficial de corante / Abstract: This study was verified the roughness, stain over composites surfaces and the relationship between of both when three finish/polishing techniques was applied. The surface analysis was obtained with a perfilometer and spectrophotometer method. The data was analysed by Kruskal-Wallis test. The statistical analysis showed that the same finish/polishing technique produced different scores of roughness (Ra) over the composites surfaces; that the same composite submited at different finish/polishing techniques could show different scores of Ra; that the best finish/polishing technique was obtained with the Sof-Lex discs and with Diamond Points the worse. Different composites could produced equivalent stain scores independently of finish/polishing techniques; different finish/polishing techniques could produced different stain level over the surface of the same composite; Sof-Lex discs produced, except for TPH composite, the minor stain level. There wasn't a direct relationship between roughness and stain levels / Tese (livre-docencia) - Univer / Livre docente em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290523 |
| Date | 24 July 2018 |
| Creators | Lovadino, José Roberto, 1953- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, informado, Não |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 101 f., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds