Tese (livre-docencia) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T15:45:44Z (GMT). No. of bitstreams: 1
CorrerSobrinho_Lourenco_LD.pdf: 2684391 bytes, checksum: 23bda3dc9540185b8d4f1f521cc36aa9 (MD5)
Previous issue date: 1998 / Resumo: O propósito deste estudo foi investigar a influência das resistências à fratura e à fadiga (a seco e em água destilada) das cerâmicas In Ceram, OPC¿e IPS Empress, fixadas com os cimentos de fosfato de zinco e ionômero de vidro. Cinqüenta e dois corpos-de-prova com 8 mm de diâmetro por 8,5 mm de altura foram confeccionados para cada tipo de cerâmica. Após aplicação do glaze, as coroas foram fixadas sobre os troqueis de metal com os cimentos de fosfato de zinco e ionômero de vidro. Em seguida, os corpos-de-prova foram armazenados em água destilada por 24 horas em temperatura ambiente antes dos ensaios. Para cada sistema e cimento (fosfato de zinco ou ionômero de vidro), dez corpos-de-prova foram submetidos ao teste de fratura a uma velocidade de 1,0 mm/min.. O segundo grupo foi submetido ao teste de fadiga por 10.000 ciclos, com carga mínima e máxima de 20 e 300 N, aplicada com força em forma sinosoidal com 1 HZ, seguido pelo de fratura em água destilada (8 corpos-de-prova para cada tipo de cimento e cerâmica) e o terceiro grupo em ambiente seco (8 corpos-de-prova para cada tipo de cimento e cerâmica), usando uma máquina Instron. Os resultados foram estatisticamente analisados pelo teste de Mann-Whitney. Os resultados indicaram que (1) - a resistência à fratura para a cerâmica In Ceram com os dois tipos de cimentos foi significantemente superior em relação às OPC¿ e IPS Empress (p<0,05); e nenhuma diferença foi encontrada entre OPC¿ e IPS Empress (2) - quando submetida à fadiga em ambiente seco, In Ceram fixada com inômero de vidro foi significantemente superior em relação à OPC¿ e IPS Empress (p<0,05); e as mesmas diferenças estatísticas foram encontradas quando os corpos-de-prova foram submetidos à fadiga em água destilada; (3) - para os fixados com fosfato de zinco e submetidos à fadiga, In Ceram e OPC¿ a seco foram estatisticamente superiores em relação à IPS Empress (p<0,05); e nenhuma diferença foi encontrada entre In Ceram e OPC¿; (4) -houve uma significante diminuição de resistência para In Ceram e IPS Empress submetidas ao teste de fadiga em água destilada, fixadas com ionômero de vidro, quando comparadas com o teste de fratura; nenhuma diferença foi encontrada quando comparada a seco; e nenhuma diferença foi encontrada para o sistema OPC¿; (5) - nos três sistemas fixados com o cimento de fosfato de zinco houve uma significante diminuição de resistência após o teste de fadiga a seco e em água destilada, quando comparada com o teste de fratura (p<0,05); e para os corpos-de-prova submetidos ao teste de fadiga, o ambiente seco apresentou valores superiores em relação às imersas em água destilada, mas nenhuma diferença estatística foi encontrada / Abstract: The aims of this paper was to investigate the influencia of fatigue, on the fracture strength of In ceram, OPC¿ and IPS Empress in both wet and dry environments, luted with zinc phosphate and glass ionomer cements. Fifty two crowns shapes with 8mm in diameter and 8.5mm height were fabricated for each ceramic system. After glazing, the crown shapes were cemented onto identical brass dies with zinc phosphate and glass ionomer cements. After, the specimens were then stored in distilled water at room temperature for 24 hours before testing. For each ceramic system luted with zinc phosphate and glass ionomer cement, ten specimens were tested for fracture strength without fatiguing at a crosshead speed of 1.0 mm per minute. The second group was submitted to a fatigue for 10,000 cycles, with minimum and maximum load of 20 and 300 N applied with the force profile in the form of a sine wave at 1 HZ, and fracture test in wet (8 specimens for each kind of ceramics and cement) and third group in a dry (8 specimens for each kind of ceramics and cement) environment; using a an Instron testing machine. The results were statistically analysed using a Mann-Whitney. The results indicated that (1) - the fracture strength for In ceram using luted zinc phosphate and glass ionomer was significantly stronger than OPC¿ and IPS Empress (p<0.05); (2) - when fatigued in a dry environment, In ceram crown shapes, luted with glass ionomer, were significantly stronger than OPC¿ and IPS Empress (p<0.05). The same statistical differences were found when fatigued in a wet environment; (3) - for luted with zinc phosphate, when fatigued in a dry environment, In ceram and OPC¿ were significantly stronger than IPS Empress (p<0.05); (4) - fatinguing and fracture testing showed a significant decrease in the frature strength for In ceram e IPS Empress in wet environment and no difference was found in dry environment. No difference was found for OPC¿; (5) -the strength of the three ceramic systems, luted with zinc phosphate, decreased significantly after fatiguing in both dry and wet environments, compared with non fatigued. No difference was found between fatiguing in dry and wet environments / Tese (livre-docencia) - Univer / Materiais Dentarios / Livre-Docente em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290622 |
| Date | 03 August 2018 |
| Creators | Correr Sobrinho, Lourenço, 1960- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, informado, Não |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 124f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds