CoordenaÃÃo de AperfeiÃoamento de Pessoal de NÃvel Superior / No presente trabalho, nanopartÃculas de M0,5Zn0,5Fe2O4 (M= Ni ou Mn) foram preparadas por sÃntese hidrotÃrmica sob condiÃÃes brandas sem qualquer procedimento de calcinaÃÃo. Amostras de composiÃÃo MFe2O4 (M = Zn, Ni ou Mn) tambÃm foram sintetizadas para fins de comparaÃÃo. As propriedades estruturais e magnÃticas das amostras foram investigadas por DifraÃÃo de Raios-X (DRX), Espectroscopia na RegiÃo do Infravermelho com Transformada de Fourier (FTIR), Espectroscopia Raman, Espectroscopia MÃssbauer, MagnetÃmetro de Amostra Vibrante (VSM) e Microscopia EletrÃnica de TransmissÃo (TEM). As anÃlises de DRX exibiram picos caracterÃsticos da fase de espinÃlio em todas as amostras sintetizadas. O tamanho mÃdio de partÃcula foi obtido por DRX, VSM e TEM e apresentou valor em torno de 10 nm para o M0,5Zn0,5Fe2O4. As imagens de TEM exibiram nanopartÃculas de morfologia cÃbica. Os parÃmetros magnÃticos observados por MÃssbauer e VSM mostraram comportamento superparamagnÃtico para todas as amostras contendo Zn, alÃm de altos valores de magnetizaÃÃo de saturaÃÃo (~55 meu/g) para a amostra Ni0,5Zn0,5Fe2O4. Devido a isto, este nÃcleo magnÃtico foi escolhido para a formulaÃÃo do nanocarreador. Desta forma, este foi inicialmente modificado com Ãcido olÃico. As anÃlises de TG e FTIR evidenciaram a presenÃa de molÃculas de oleato na superfÃcie da nanopartÃcula. AlÃm disso, o coeficiente de revestimento do processo realizado foi 3,7 oleato / nm2. Um estudo de adsorÃÃo da piplartina na nanopartÃcula modificada (NiZn-AO) foi realizado e observou-se relaÃÃo (NiZn-AO : Piplartina) Ãtima de 1 : 2 (m/m). ApÃs o processo adsortivo, o sistema contendo NiZn-AO e piplartina foi revestido com matriz polimÃrica constituÃda de P123 e F127 para conferir biocompatibilidade ao sistema, e formar o nanocarreador. Testes preliminares de hipertermia foram realizados na nanopartÃcula e observou-se que um campo de 126 Oe conduz a geraÃÃo de calor para alcanÃar uma temperatura de 42ÂC, dentro da faixa de hipertermia moderada. Portanto, o nanocarreador formulado apresenta potencial para aplicaÃÃes biomÃdicas. / In this work, nanoparticles of the M0,5Zn0,5Fe2O4 (M = Ni ou Mn) have been prepared by hydrothermal synthesis in mild conditions without any calcinations process. MFe2O4 (M = Zn, Ni or Mn) nanoparticles were also prepared for comparison. The structural and magnetic properties of the ferrites were investigated by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, MÃssbauer spectroscopy, vibrating sample magnetometer (VSM) and Transmission electron microscopy (TEM). XRD analysis showed peaks of the spinel phase for all samples. The average particle size was obtained by XRD, TEM and VSM and values around 10 nm were found for M0,5Zn0,5Fe2O4. TEM images showed particles of cubic morphology. The magnetic parameters observed by MÃssbauer and VSM shown superparamagnetic behavior for the samples containing Zn and high saturation magnetization values (~55 emu/g) for Ni0,5Zn0,5Fe2O4. Due to this, it was chosen for formulating the nanocarrier. Thus, it was first modified with oleic acid. The TG and FTIR analysis revealed the presence of oleate molecules on the surface of the nanoparticle. Furthermore, the coating coefficient of the process carried was 3.7 oleate / nm2. A study of piplartine adsorption on the modified nanoparticle (NiZn-AO) was performed and the optimum relationship (NiZn-AO: piplartine) was 1 : 2 (w / w). After the adsorptive process, the system containing NiZn-AO and piplartine was coated with polymeric matrix consisting of F127 and P123 to confer biocompatibility to the system and form the nanocarrier. Hyperthermia tests were performed in nanoparticles and it was observed that a field of 126 Oe leads to heat generation to attain a temperature of 42ÂC within the range of moderate hyperthermia. Therefore, the fabricated nanocarrier had potential for biomedical applications.
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:5864 |
| Date | 17 August 2012 |
| Creators | Rafael Melo Freire |
| Contributors | Pierre BasÃlio Almeida Fechine, Tamara GonÃalves AraÃjo, EdÃsia Martins Barros de Sousa |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em QuÃmica, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds