Estudo da degradaÃÃo de policarbonato de bisfenol A (PCBFA) de garrafÃes de Ãgua mineral / Study on the degradation of bisphenol A polycarbonate (PCBFA) bottles of mineral water

Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / O policarbonato de bisfenol A (PCBFA) à um poliÃster, com repetiÃÃo de estrutura quÃmica das molÃculas de bisfenol A (BFA), que acumula um conjunto bem balanceado de propriedades, tais como: transparÃncia, estabilidade tÃrmica e dimensional, resistÃncia mecÃnica, antichama; permitindo classificÃ-lo como plÃstico de engenharia. Ele à um material utilizado em garrafÃes retornÃveis para acondicionamento de Ãgua mineral. O processo de fabricaÃÃo dos garrafÃes à de grande importÃncia, pois objetiva a produÃÃo de um material uniforme, que de certa maneira garante qualidade para resistir Ãs intempÃries do tempo e aos diversos processos de envasamento de Ãgua, estocagem e distribuiÃÃo. Os ÃrgÃos governamentais regulamentaram que o tempo de vida Ãtil das embalagens à somente de trÃs anos. A validade da Ãgua em garrafÃes lacrados varia de 60 a 120 dias. Depois de aberto, a recomendaÃÃo à consumir em atà duas semanas. A degradaÃÃo do PCBFA foi estudada utilizando garrafÃes de 20 litros de diferentes anos de fabricaÃÃo (0-15 anos), observou-se o efeito do tempo na mudanÃa das caracterÃsticas e propriedades do material. Verificou-se que a espessura dos garrafÃes diminui com o tempo de fabricaÃÃo. A partir de 8 anos de fabricaÃÃo, possÃveis mudanÃas estruturais, como a descarboxilaÃÃo, diminuiÃÃo da temperatura de transiÃÃo vÃtrea e alteraÃÃo nas propriedades mecÃnicas foram constatadas atravÃs das tÃcnicas de infravermelho (FTIR), Calorimetria ExploratÃria Diferencial (DSC) e por ensaios mecÃnicos de traÃÃo, respectivamente. Por microscopia eletrÃnica de varredura (MEV), verificou-se que a superfÃcie externa apresentou-se com mais alteraÃÃes morfolÃgicas em relaÃÃo à superfÃcie interna. Por anÃlise termogravimÃtrica (TGA), notou-se que o PCBFA da superfÃcie interna tem uma menor estabilidade tÃrmica que a superfÃcie externa do garrafÃo. Por anÃlise de fluorescÃncia foi detectada a presenÃa de BFA em Ãgua destilada mantida em contato com o garrafÃo estocada durante 2 meses. O BFA à o reagente utilizado na sÃntese industrial do PCBFA onde o mesmo à um desregulador endÃcrino que causa alteraÃÃes hormonais no sistema endÃcrino. Pode-se concluir que os garrafÃes de PCBFA sofrem degradaÃÃo com o passar dos anos a ponto do material perder suas principais propriedades, tanto na superfÃcie externa e interna. A relevÃncia maior do estudo evidencia sobre a validade dos garrafÃes e a possÃvel liberaÃÃo de BFA na Ãgua. / The polycarbonate of bisphenol A (PCBFA) is a polye
ster with repeating chemical
structure of molecules of bisphenol A (BFA), which
accumulates a well-balanced set of
properties, such as transparency, thermal and dimen
sional stability, mechanical strength,
flame retardant; allowing classify it as engineerin
g plastic. It is a material used in
returnable carboys for packaging of mineral water.
The manufacturing process of the
carboys is of great importance, because it aims the
production of a uniform material,
which somehow ensures quality to withstand the incl
ement weather of weather and the
various processes of potting water, stocking and di
stribution of carboys. Government
agencies have regulated that the time of validity o
f the carboys is only three years. The
validity of water in sealed bottles ranges from 60
to 120 days. Once opened, the
recommendation is to consume within two weeks. The
degradation was studied using
PCBFA of 20 liters carboys of different fabrication
years (0-15 years), we observed the
effect of time in changing of the characteristics a
nd properties of material. It was found
that the thickness of carboys lowers with time of f
abrication. From 8 years of
manufacturing, possible structural changes, such as
decarboxylation, reduction in glass
transition temperature and changes in mechanical pr
operties were observed via infrared
techniques (FTIR), differential scanning calorimetr
y (DSC) and tensile test,
respectively. By scanning electron microscopy, it w
as found that the external surface
appeared with more morphological changes in relatio
n to the inner surface. By
thermogravimetric analysis (TGA), it was noted that
the PCBFA the inner surface has a
lower thermal stability than the outer surface of t
he carboy. By fluorescence analysis,
we detected the presence of BFA in distilled water
kept in contact with the stored
carboy for 2 months. BFA is the reagent used in the
industrial synthesis of PCBFA
where it is an endocrine disrupter which causes hor
monal changes in the endocrine
system. It can be concluded that the polycarbonate
carboys undergo degradation with
passing of the years to the point of the material l
osing its main properties, both the outer
and inner surface. The most relevant study demonstr
ates the validity of carboys and the
possible release of BFA in the water

Identiferoai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:5873
Date30 August 2012
CreatorsFabricio Siqueira Queiroz
ContributorsJudith Pessoa de Andrade Feitosa, Regina CÃlia Monteiro de Paula, Antonio Savio Gomes MagalhÃes
PublisherUniversidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em QuÃmica, UFC, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0017 seconds