Conselho Nacional de Desenvolvimento Científico e Tecnológico / Este estudo avaliou o efeito de diferentes métodos de silanização e aplicação do ácido hidrofluorídrico (HF) sobre a resistência à microtração de uma cerâmica de dissilicato de lítio a um cimento resinoso. Quarenta blocos de IPS e.max Press /Ivoclar Vivadent (5x5x6mm) foram cimentados a blocos de resina Z250/3M ESPE (5x5x6mm) usando o cimento resinoso RelyX ARC/3M ESPE de acordo com os seguintes métodos de tratamento superficial: G1: 20s de ácido fluorídrico (HF) + silano não hidrolisado Primer-Activactor/Dentsply (SNH) seco à temperatura ambiente; G2: 20s HF + silano pré-hidrolisado RelyX Ceramic-Primer/3M ESPE (SPH) seco à temperatura ambiente; G3: 10s HF + SNH seco com ar quente (50oC-2min); G4: 10sHF + SPH seco com ar quente (50oC-2min); G5: sem ácido, SNH seco com ar quente (50oC-2min); G6: sem ácido, SPH seco com ar quente (50oC-2min); G7: sem ácido, SNH seco à temperatura ambiente; G8: sem ácido, SPH seco à temperatura ambiente. Antes de cada método de silanização, os blocos cerâmicos receberam acabamento com lixas de carbeto de silício (220-600) e limpeza com ácido fosfórico 37% (1min). A cimentação foi realizada com carga vertical de 1kg por 10min. Os conjuntos de cerâmica/cimento/resina foram armazenados em água destilada (37C) por 24 horas e depois seccionados em máquina de corte Isomet 1000 a fim de obter palitos (n = 40) de 1mm2 de área da seção transversal, que foram submetidos ao teste de microtração em máquina de ensaio universal Emic (v = 0,5mm/min). O modo de fratura foi avaliado em microscópio eletrônico de varredura. A análise estatística foi realizada utilizando ANOVA / Dunnett (p-valor = 0,000). As médias MPa e desvio padrão foram: G1-21,5 (8,9) BC; G2-30,5 (7,2) A; G3-19.4 (9.1) BC; G4-24,0 (9,0) B; G5-8.1 (3.2) D; G6 -18,0 (6,2) C; G7-7.8 (2,6) D; G8-6.3 (2,5) D. Grupos 2, 3, 4 e 6 não tiveram falhas prematuras dos palitos contra os grupos 1, 5, 7 e 8, que apresentaram 2,2; 44,4; 75,6 e 33,3% de perdas prematuras, respectivamente. O teste de correlação foi realizado apresentando significância estatística, com valor de -0,736 (p-valor = 0,000), mostrando que, a medida que o percentual de perda prematura aumenta, a média da MPa diminui. Quanto ao modo de fratura, observou-se 44,97% de falhas do tipo mista, 51,70% de falhas do tipo adesiva, 3,33% de falhas do tipo coesiva do cimento. Quando é realizada a supressão do condicionamento com HF como pré-tratamento da superfície cerâmica IPS e.max Press, a aplicação de silano SPH, associada ao seu tratamento térmico, deve ser o método de silanização recomendado, embora os valores mais elevados de resistência de união tenham sido os obtidos quando utilizado o condicionamento com HF por 20s. Quando é realizada a redução do tempo de condicionamento com HF para 10s, a aplicação do silano (SPH ou SNH) deve ser sempre associada ao seu tratamento térmico. O SNH só deve ser usado se as superfícies das cerâmicas IPS e.max Press forem tratadas com HF. / This study devaluated the effect of different types of silanization and hydrofluoric acid on the microtensile bond strength of a lithium dissilicate ceramic system. Forty IPS e.max Press /Ivoclar Vivadent blocks (5x5x6mm) were cemented to Z250/3M ESPE resin blocks (5x5x6mm) using RelyX ARC/3M ESPE resin-cement according to the following silanization methods: G1: 20s hydrofluoric acid (HF) + non-hydrolyzed silane Primer-Activactor/Dentsply (NHS) dried at room temperature; G2: 20sHF + pre-hydrolyzed silane RelyX Ceramic-Primer/3M ESPE (PHS) dried at room temperature; G3: 10sHF + NHS dried with hot air (50oC-2min); G4: 10sHF + PHS + hot air; G5: NHS + hot air; G6: PHS + hot air; G7: NHS dried at room temperature; G8: PHS dried at room temperature. Before each silanization method, all ceramic blocks were abraded with SiC grit papers (220-600) and cleaned with 37% phosphoric acid (1min). The cementation was made with vertical load of 01 kg for 10 min. After cementation procedure, all ceramic/ciment/resin blocks were stored in distilled water (37oC) for 24h before being cut to obtain stick-shapped specimens (n=45) of approximately 1mm2 cross-sectional area for microtensile test (v=0.5mm/min). Statistical analysis was performed using ANOVA/Dunnett (p-value = 0,000). The mean MPa(SD) values were: G1-21.5(8.9)BC; G2-30.5(7.2)A; G3-19.4(9.1)BC; G4-24.0(9.0)B; G5-8.1(3.2)D; G6-18.0(6.2)C; G7-7.8(2.6)D; G8-6.3(2.5)D. Groups 2, 3, 4 and 6 had no sticks premature fail against groups 1, 5, 7 and 8, that had 2.2, 44.4, 75.6 and 33.3% of sticks premature fails, respectively. As the correlation coefficient was statistically significant, -0.736 (p-value = 0.000), it could be argued that as the percentage of premature loss increased the MPa mean decreases. The failure mode was 44.97% of mixed failures, 51.70% of adhesive failures, 3.33% of cohesive failures of the cement. When the pretreatment is performed without HF conditioning of the IPS e.max Press ceramic surface, then PHS with hot air application should be the silanization method recommended, although higher bond strength values were obtained when HF conditioning for 20s was used with this type of silane. When the time of HF conditioning is reduced for 10 sec, the application of silane (SPH or SNH) must be always related to its heat treatment. NHS should only be used if IPS e.max Press ceramic surfaces are treated with HF.
| Identifer | oai:union.ndltd.org:IBICT/urn:repox.ist.utl.pt:BDTD_UERJ:oai:www.bdtd.uerj.br:4124 |
| Date | 24 August 2012 |
| Creators | Leticia Monteiro Peixoto |
| Contributors | Hélio Rodrigues Sampaio Filho, Eduardo Batitucci, Marco Antônio Masioli, Eduardo Moreira da Silva, Angela Alexandre Meira Dias, Claudia Batitucci dos Santos Daroz |
| Publisher | Universidade do Estado do Rio de Janeiro, Programa de Pós-Graduação em Odontologia, UERJ, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UERJ, instname:Universidade do Estado do Rio de Janeiro, instacron:UERJ |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds