A new technique based on the study of the transmitted neutron beam has been developed to study the low-temperature decomposition of austenite in a 0.4 wt.% C–3 wt.% Mn–2 wt.% Si steel. Experiments were conducted in which the neutron beam continuously passed through a specially designed layered sample, the temperature of which could be controlled to allow for a high-temperature austenization treatment followed by accelerated cooling to an isothermal transformation temperature in the range of 275–450 °C. It was possible to measure the volume fraction of the face-centred cubic (fcc) and body-centred cubic (bcc) phases and the carbon concentration of the fcc phase by characterizing the neutron Bragg edges in the transmitted beam. This provides a technique for in situ continuous measurements on the decomposition of austentite. The technique has been validated by comparing the data with other experimental techniques such as dilatometry, quantitative optical metallography and room temperature X-ray diffraction.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:BVAU.2429/397 |
| Date | January 2007 |
| Creators | Poole, Warren J., Militzer, Matthias, Huang, J., Vogel, S. C., Jacques, C. |
| Publisher | Elsevier |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | English |
| Detected Language | English |
| Type | text |
Page generated in 0.0017 seconds