A numerical model for solid oxide fuel cells with Ni-infiltrated porous anode has been described. The novel contribution of the work is the development of a semi-continuous film model to describe the infiltrated Ni-phase. This model relates experimentally controllable parameters, namely, Ni- loading, porosity and pore size to the effective electronic conductivity of the Ni-phase and the number of active reaction sites or the triple phase boundary (TPB). The semi-continuous film model was incorporated in a two-dimensional (2D) SOFC model. The 2D model considers the coupled gas-phase transport, charge transport and electrochemical kinetics to directly examine the effect of Ni loading and porosity on the electrochemical performance of Ni-infiltrated SOFC anodes. From the semi-continuous film model, an optimal Ni loading that corresponds to a maximum in TPB length was identified. Comparison of effective electronic conductivity and TPB length for a Ni-infiltrated anode with those for a composite Ni-YSZ anode suggests that an infiltrated Ni anode with adequate electrical conductivity and sufficiently high TPB length can be fabricated even at a very low Ni loading. Comparison of various porous anodes with varying Ni loading, it was determined that maximum electrochemical performance does indeed correspond to anode with maximum TPB length. It was also determined that an infiltrated anode will have higher performance capabilities when compared to the conventional composite electrodes. However, degradation of performance may result due to degradation of connectivity in the infiltrated Ni. The methodology to model the latter effect was also proposed. / Thesis (Master, Chemical Engineering) -- Queen's University, 2012-06-13 13:09:49.182
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OKQ.1974/7278 |
| Date | 14 June 2012 |
| Creators | HARDJO, ERIC FREDDY |
| Contributors | Queen's University (Kingston, Ont.). Theses (Queen's University (Kingston, Ont.)) |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | English, English |
| Detected Language | English |
| Type | Thesis |
| Rights | This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner. |
| Relation | Canadian theses |
Page generated in 0.0022 seconds