The compatibility properties of some contemporary finish coats together with their complementary layers used in insulated exterior walls were examined in terms of water vapour permeability and modulus of elasticity.
Basic physical and mechanical properties of some synthetic-, cement- and polymer-based external finish coats were analyzed in laboratory. Some additional samples, complementing the wall section, were also examined for their water vapour permeability.
Results showed that the finish coats were high vapour permeable although they had high resistance to water vapour permeation, which was achieved by their application in thin layers. Cement-based undercoats were found to be medium permeable. The application of primer and/or paint was found to decrease the permeability of finish coats in different ranges. Thermal insulation layer was found to interrupt water vapour flow considerably. Among polystyrene- and mineral-wool-based thermal insulation boards, rockwool was recommended as the insulation layer due to its medium vapour permeability. In conclusion, walls insulated externally with rockwool boards and plastered with polymer-based finish coat, FC8ACB or synthetic-based finish coat FC3SB were found to be the most proper combination in terms of breathing and thermal resistance capabilities. All finish coats seemed to have sufficient strength and except the synthetic-based finish coat, FC2SB, they seemed to be compatible with each other and with the masonry in terms of their Emod values. Further studies were recommended on some other compatibility properties of finishing systems, such as thermal and moisture dilatation properties, and on the relation between the resistance to water vapour permeation and water permeability.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12607741/index.pdf |
| Date | 01 September 2006 |
| Creators | Ors, Kerime |
| Contributors | Tavukcuoglu, Ayse |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0089 seconds