ABSTRACT
INTERACTION BETWEEN MICRO AND NANO PATTERNED
POLYMERIC SURFACES AND DIFFERENT CELL TYPES
Ö / zç / elik, Hayriye
Ph.D., Department of Biology
Supervisor: Prof. Dr. Vasif Hasirci
Co-Supervisor: Dr. Celestino Padeste
August 2012, 139 pages
Micro and nanopatterned surfaces are powerful experimental platforms for investigating the
mechanisms of cell adhesion, cell orientation, differentiation and they enable significant
contributions to the fields of basic cell and stem cell biology, and tissue engineering. In this
study, interaction between micro and nanopatterned polymeric surfaces and different cell
types was investigated. Three types of micropillars were produced by photolithography
(Type 1-3), while nanometer sized pillars were produced in the form of an array by electron
beam lithography (EBL). Replica of silicon masters were made of polydimethylsiloxane
(PDMS). Polymeric [P(L-D,L)LA and a P(L-D,L)LA:PLGA blend] replica were prepared by
solvent casting of these on the PDMS template and used in in vitro studies. The final
substrates were characterized by various microscopic methods such as light microscopy,
atomic force microscopy (AFM) and scanning electron microscopy (SEM).
In order to investigate deformation of the nucleus in response to the physical restrictions
imposed by micropillars, Type 1 and Type 2 pillars were used. These substrates were
covered with pillars with different interpillar distances. While Type 1 is covered with
symmetrically (in X-Y directions) distributed pillars, Type 2 pillars were distributed
asymmetrically and the inter-pillar distances were increased. Nuclei deformation of five cell
v
types, two cancer cell lines (MCF7 and Saos-2), one healthy bone cell (hFOB1.19), one
stem cell (bone marrow origined mesemchymal stem cells, BMSCs) and one standard
biomaterial test cell type, (L929) fibroblasts was examined by using fluorescence
microscopy and SEM. The nuclei of Saos-2 and MCF7 cells were found to be deformed most
drastically. Nucleus deformation and intactness of nuclear membrane was examined by Anti-
Lamin A staining. The interaction of the cells with micropillars was visualized by labelling
focal adhesion complexes (FAC). Wettabilities of patterned and smooth surfaces were
determined. As the patterns become denser (closer micropillars, Type 1) the hydrophobicity
increased. Similar to water droplets, the cells were mostly spread at the top of the Type 1
pillars. The number of cells spread on the substrate surface was much higher on Type 2
patterned films. In order to support these qualitative findings, nucleus deformation was
quantified by image analysis. Frequency of nucleus deformation was determined as the ratio
of deformed to the total number of nuclei (%). In order to quantify the intensity of nuclei
deformation, their circularity was evaluated. In addition to nucleus deformation, alterations in
the ratio of cell area-to-nucleus area in response to micropillars were determined by image
analysis. The results indicated that cancerous cells were more deformable. The qualitative
microscopic evaluation and the data obtained by quantification of the nucleus and cellular
deformation were in good agreement. In addition, the findings were consistent with
expectations which suggest that cancerous cells are &ldquo / softer&rdquo / .
In the second part of the research the force applied by the cells on arrays of micropillars with
high aspect ratios (Type 3 substrates) during tugging at the pillars was investigated.
Micropillars were produced using P(L-D,L)LA as well as a 60:40 blend of P(L-D,L)LA with
PLGA. The blend is a material with lower stiffness than P(L-D,L)LA. The mechanical
properties of the two materials were determined by tensile testing of solvent cast films.
Deformation of Type 3 micropillars by the cellular tugging force of Saos-2 and L929 was
studied by fluorescence and SEM microscopy, both on stiff and softer substrates.
Displacements of the centers nodes of the pillars were evaluated from SEM micrographs. On
the stiff surface, the two cell types bent the pillars to the same extent. On the other softer
substrate (blends), however, the maximum displacements observed with Saos-2 cells were
higher than the ones caused on the stiffer substrate or the ones caused by L929 cells. It is
reported that stiffness of the substrate can determine stem cell lineage commitment. In order
to examine the effects of change of substrate stiffness on osteogenic differentiation of
BMSCs, osteopontin (OPN) expression was determined microscopically. It was found that
osteogenic differentiation is enhanced when BMSCs are cultured on P(L-D,L)LA Type 3
pillars.
vi
In the last part of research, arrays of nanopillars whose interpillar distances systematically
varied to form different fields were examined in terms of adhesion and alignment in order to
determine the differential adhesion of BMSCs and Saos-2 cells. The difference in their
adhesion preference on nanopillar arrays was quantified by image analysis. It was observed
that BMSCs and Saos-2 cells behaved in an opposite manner with respect to each other on
the fields with the highest density of nanopillars. The BMSCs avoided the most densely
nanopillar covered fields and occupied the pattern free regions. The Saos-2, on the other
hand, occupied the most densely nanopillar covered fields and left the pattern free regions
almost unpopulated. It was also found that both BMSCs and Saos-2 cells aligned in the
direction of the shorter distance between the pillars. Both BMSCs and Saos-2 cells started to
align on the pillars if the distance in any direction was > / 1.5 &mu / m. To better understand the
effects of chemical and physical cues, protein coating and material stiffness were tested as
two additional parameters. After fibronectin coating, the surfaces of P(L-D,L)LA films with the
highly dense pillar covered fields, which were avoided when uncoated, were highly
populated by the BMSC. Similarly, decreasing the stiffness of a surface which was normally
avoided by the BMSCs made it more acceptable for the cells to attach.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12614798/index.pdf |
| Date | 01 October 2012 |
| Creators | Ozcelik, Hayriye |
| Contributors | Hasirci, Vasif |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | Ph.D. Thesis |
| Format | text/pdf |
| Rights | Access forbidden for 1 year |
Page generated in 0.0028 seconds