The effect of Ni and Ni(Pt) alloy with ~5 and 10 at. % Pt on the agglomeration and Ge out-diffusion in Nickel germanosilicide formed on Si₀.₇₅Ge₀.₂₅(100) has been studied. A remarkable improvement in the agglomeration behavior with increasing Pt atomic percentage is observed by sheet resistance measurements and scanning electron microscopy (SEM). In addition, x-ray diffraction (XRD) shows that only NiSiGe or Ni(Pt)SiGe phase exists from 400 to 800°C. However, Ge out-diffusion from the monogermanosilicide grains is obvious at 600°C and 700°C for Ni/SiGe and Ni(Pt)(Pt at.%~10%)/SiGe, respectively, evident by XRD and micro-Raman spectroscopy. The improved melting temperature of Ni(Pt)SiGe solution compared to that of NiSiGe is the likely reason of seeing better surface morphology and suppressing Ge out-diffusion of the germanosilicide grains observed. / Singapore-MIT Alliance (SMA)
| Identifer | oai:union.ndltd.org:MIT/oai:dspace.mit.edu:1721.1/3825 |
| Date | 01 1900 |
| Creators | Jin, Lijuan, Pey, Kin Leong, Choi, Wee Kiong, Fitzgerald, Eugene A., Antoniadis, Dimitri A., Chi, D.Z. |
| Source Sets | M.I.T. Theses and Dissertation |
| Language | en_US |
| Detected Language | English |
| Type | Article |
| Format | 1019837 bytes, application/pdf |
| Relation | Advanced Materials for Micro- and Nano-Systems (AMMNS); |
Page generated in 0.0025 seconds